Electrochemical Properties of Tin Sulfide Nano-Sheets as Cathode Material for Lithium-Sulfur Batteries

Creators

  • 1. Shenzhen University
  • 2. University of Azad Jammu and Kashmir
  • 3. Abdus Salam Centre for Physics
  • 4. Mirpur University of Science and Technology
  • 5. Xi'an Jiaotong University
  • 6. Northwestern Polytechnical University

Description

Unprecedented self-assembled hierarchical nano-sheets of SnS were synthesized by the hydrothermal method. In a typical reaction, SnCl2.2H2O and Na2S.9H2O were used as reactants. Structural and morphological properties were studied by X-ray diffraction (XRD), and scanning electron microscopy (SEM) while the electrochemical properties were measured by cyclic voltammetry, charge-discharge cycles, and electrochemical impedance spectroscopy (EIS). SEM results showed the 1-D SnS nano-sheets with an average thickness of around 20 nm. Cyclic voltammogram and charge-discharge spectra showed good cycling stability. All these results showed that SnS nano-sheets are promising candidate material to be used as electrode for Li-S batteries.

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

تم تصنيع أوراق النانو الهرمية غير المسبوقة التي تم تجميعها ذاتيًا من SnS بواسطة الطريقة الحرارية المائية. في تفاعل نموذجي، تم استخدام SnCl2.2H2O و Na2S.9H2O كمواد متفاعلة. تمت دراسة الخصائص الهيكلية والمورفولوجية عن طريق حيود الأشعة السينية (XRD)، والمسح المجهري الإلكتروني (SEM) بينما تم قياس الخصائص الكهروكيميائية عن طريق قياس الفولتية الدوري، ودورات الشحن والتفريغ، والمعاوقة الكهروكيميائية الطيفية (EIS). أظهرت نتائج SEM أوراق نانو SnS أحادية الأبعاد بسماكة متوسطة تبلغ حوالي 20 نانومتر. أظهر الفولتاموجرام الدوري وأطياف تفريغ الشحنة استقرارًا جيدًا في الدورة. أظهرت كل هذه النتائج أن أوراق النانو SnS هي مادة مرشحة واعدة لاستخدامها كقطب كهربائي لبطاريات Li - S.

Translated Description (French)

Des nanofeuilles hiérarchiques de SnS auto-assemblées sans précédent ont été synthétisées par la méthode hydrothermale. Dans une réaction typique, SnCl2.2H2O et Na2S.9H2O ont été utilisés comme réactifs. Les propriétés structurales et morphologiques ont été étudiées par diffraction des rayons X (DRX) et microscopie électronique à balayage (MEB), tandis que les propriétés électrochimiques ont été mesurées par voltamétrie cyclique, cycles de charge-décharge et spectroscopie d'impédance électrochimique (EIS). Les résultats du MEB ont montré les nanofeuilles 1-D SnS avec une épaisseur moyenne d'environ 20 nm. Le voltammogramme cyclique et les spectres de charge-décharge ont montré une bonne stabilité cyclique. Tous ces résultats ont montré que les nanofeuilles de SnS sont un matériau candidat prometteur pour être utilisé comme électrode pour les batteries Li-S.

Translated Description (Spanish)

Se sintetizaron nanohojas jerárquicas de SnS autoensambladas sin precedentes mediante el método hidrotérmico. En una reacción típica, se utilizaron SnCl2.2H2O y Na2S.9H2O como reactivos. Las propiedades estructurales y morfológicas se estudiaron mediante difracción de rayos X (XRD) y microscopía electrónica de barrido (SEM), mientras que las propiedades electroquímicas se midieron mediante voltametría cíclica, ciclos de carga-descarga y espectroscopía de impedancia electroquímica (EIS). Los resultados de SEM mostraron las nano-láminas 1-D SnS con un espesor medio de alrededor de 20 nm. El voltamograma cíclico y los espectros de carga-descarga mostraron una buena estabilidad cíclica. Todos estos resultados mostraron que las nano-láminas de SnS son un material candidato prometedor para ser utilizado como electrodo para baterías de Li-S.

Files

pdf.pdf

Files (882.2 kB)

⚠️ Please wait a few minutes before your translated files are ready ⚠️ Note: Some files might be protected thus translations might not work.
Name Size Download all
md5:36d8b4f84182600768aef3c7e3605e72
882.2 kB
Preview Download

Additional details

Additional titles

Translated title (Arabic)
الخصائص الكهروكيميائية للصفائح النانوية لكبريتيد القصدير كمادة كاثودية لبطاريات الليثيوم والكبريت
Translated title (French)
Propriétés électrochimiques des nano-feuilles de sulfure d'étain en tant que matériau de cathode pour les batteries lithium-soufre
Translated title (Spanish)
Propiedades electroquímicas de las nanohojas de sulfuro de estaño como material de cátodo para baterías de litio-azufre

Identifiers

Other
https://openalex.org/W3023034592
DOI
10.3389/fchem.2020.00254

Is supplement to
https://openalex.org/W4381060394 (Other)
https://openalex.org/W4362667714 (Other)
https://openalex.org/W2509298593 (Other)
https://openalex.org/W2506226718 (Other)
https://openalex.org/W2380339328 (Other)
https://openalex.org/W2252828978 (Other)
https://openalex.org/W2092816171 (Other)
https://openalex.org/W2008912847 (Other)
https://openalex.org/W1996763009 (Other)
https://openalex.org/W1976861527 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Pakistan

References

  • https://openalex.org/W1974789788
  • https://openalex.org/W1988215101
  • https://openalex.org/W2006318126
  • https://openalex.org/W2012134506
  • https://openalex.org/W2033788636
  • https://openalex.org/W2069912559
  • https://openalex.org/W2097924219
  • https://openalex.org/W2133719430
  • https://openalex.org/W2137469103
  • https://openalex.org/W2157344652
  • https://openalex.org/W2190051302
  • https://openalex.org/W2314151170
  • https://openalex.org/W2510111099
  • https://openalex.org/W2514308776
  • https://openalex.org/W2611716575
  • https://openalex.org/W2782004571
  • https://openalex.org/W2914424746