Effects of chitosan and Tween 80 addition on the properties of nanofiber mat through the electrospinning
Creators
- 1. King Mongkut's University of Technology Thonburi
- 2. King Mongkut's University of Technology North Bangkok
Description
Abstract Chitosan (CS) with excellent biomedical properties was mixed with polyvinyl alcohol (PVA) to be used as the spinning solution. The spinning solutions with various concentrations of CS:PVA from 10:90% to 50:50% (v/v) were investigated. Tween 80 (T80) was added in the spinning solutions of CS and PVA. The nanofiber mats with and without T80 addition obtained from the spinning solutions by electrospinning technique were investigated and addressed. The results showed that the viscosity of the CS and PVA spinning solutions increased with increasing the CS concentration, whereas the viscosity decreased after T80 addition. The nanofiber mats with 10–30% CS concentrations were prepared successfully as a smooth surface and high dense nanofiber mat. The average diameter of the nanofiber decreased with increasing the CS concentration. The increase in the CS concentration of the nanofiber mat can increase the mechanical and antibacterial properties, whereas the wettability and drug release property were decreased. Moreover, the nanofiber mats with T80 addition had higher mechanical property and wettability than the nanofiber mats without T80 addition. Finally, the T80 addition can enhance hydrophilicity and promote the drug release property of the nanofiber mat.
Translated Descriptions
⚠️
This is an automatic machine translation with an accuracy of 90-95%
Translated Description (Arabic)
تم خلط الشيتوزان المجرد (CS) ذو الخصائص الطبية الحيوية الممتازة مع كحول البولي فينيل (PVA) لاستخدامه كمحلول غزل. تم التحقيق في حلول الغزل بتركيزات مختلفة من CS:PVA من 10:90 ٪ إلى 50:50 ٪ (v/v). تمت إضافة Tween 80 (T80) في حلول الغزل لـ CS و PVA. تم فحص ومعالجة حصائر الألياف النانوية مع وبدون إضافة T80 التي تم الحصول عليها من محاليل الغزل عن طريق تقنية الغزل الكهربائي. أظهرت النتائج أن لزوجة محاليل الغزل CS و PVA زادت مع زيادة تركيز CS، في حين انخفضت اللزوجة بعد إضافة T80. تم تحضير حصائر الألياف النانوية بتركيزات 10-30 ٪ CS بنجاح كسطح أملس وحصيرة ألياف نانوية عالية الكثافة. انخفض متوسط قطر الألياف النانوية مع زيادة تركيز CS. يمكن أن تؤدي الزيادة في تركيز CS لحصيرة الألياف النانوية إلى زيادة الخصائص الميكانيكية والمضادة للبكتيريا، في حين تم تقليل خاصية قابلية الترطيب وإطلاق الدواء. علاوة على ذلك، فإن حصائر الألياف النانوية مع إضافة T80 لها خاصية ميكانيكية وقابلية ترطيب أعلى من حصائر الألياف النانوية دون إضافة T80. أخيرًا، يمكن لإضافة T80 أن تعزز الألفة للماء وتعزز خاصية إطلاق الدواء لحصيرة الألياف النانوية.Translated Description (French)
Le chitosane abstrait (CS) aux excellentes propriétés biomédicales a été mélangé à de l'alcool polyvinylique (PVA) pour être utilisé comme solution de filage. Les solutions de filage avec différentes concentrations de CS :PVA de 10:90% à 50:50% (v/v) ont été étudiées. Du Tween 80 (T80) a été ajouté dans les solutions de filage de CS et PVA. Les tapis de nanofibres avec et sans addition de T80 obtenus à partir des solutions de filage par technique d'électrofilage ont été étudiés et traités. Les résultats ont montré que la viscosité des solutions de filage CS et PVA augmentait avec l'augmentation de la concentration de CS, alors que la viscosité diminuait après l'addition de T80. Les tapis en nanofibres avec des concentrations de CS de 10–30% ont été préparés avec succès comme une surface lisse et un tapis en nanofibres très dense. Le diamètre moyen de la nanofibre diminuait avec l'augmentation de la concentration de CS. L'augmentation de la concentration en CS du tapis de nanofibres peut augmenter les propriétés mécaniques et antibactériennes, tandis que la mouillabilité et la propriété de libération du médicament ont été diminuées. De plus, les tapis en nanofibres avec addition de T80 avaient des propriétés mécaniques et une mouillabilité supérieures à celles des tapis en nanofibres sans addition de T80. Enfin, l'ajout de T80 peut améliorer l'hydrophilie et favoriser la propriété de libération de médicament du tapis de nanofibres.Translated Description (Spanish)
El quitosano (CS) con excelentes propiedades biomédicas se mezcló con alcohol polivinílico (PVA) para ser utilizado como solución de hilatura. Se investigaron las soluciones de hilado con diversas concentraciones de CS:PVA de 10:90% a 50:50% (v/v). Se añadió Tween 80 (T80) en las soluciones de hilado de CS y PVA. Se investigaron y abordaron las alfombrillas de nanofibras con y sin adición de T80 obtenidas a partir de las soluciones de hilado mediante técnica de electrohilado. Los resultados mostraron que la viscosidad de las soluciones de hilatura de CS y PVA aumentó con el aumento de la concentración de CS, mientras que la viscosidad disminuyó después de la adición de T80. Las esteras de nanofibra con concentraciones de CS del 10-30% se prepararon con éxito como una superficie lisa y una estera de nanofibra de alta densidad. El diámetro medio de la nanofibra disminuyó al aumentar la concentración de CS. El aumento en la concentración de CS de la estera de nanofibras puede aumentar las propiedades mecánicas y antibacterianas, mientras que la humectabilidad y la propiedad de liberación del fármaco disminuyeron. Además, las esteras de nanofibra con adición de T80 tenían una mayor propiedad mecánica y humectabilidad que las esteras de nanofibra sin adición de T80. Finalmente, la adición de T80 puede mejorar la hidrofilicidad y promover la propiedad de liberación de fármaco de la estera de nanofibras.Files
pdf.pdf
Files
(13.2 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:127b5d2f1151fa0ed1f84b3d695c943a
|
13.2 MB | Preview Download |
Additional details
Additional titles
- Translated title (Arabic)
- آثار إضافة الشيتوزان وتوين 80 على خصائص حصيرة الألياف النانوية من خلال الغزل الكهربائي
- Translated title (French)
- Effets de l'addition de chitosane et de Tween 80 sur les propriétés du tapis de nanofibres par électrofilage
- Translated title (Spanish)
- Efectos de la adición de quitosano y Tween 80 en las propiedades de la estera de nanofibras a través del electrohilado
Identifiers
- Other
- https://openalex.org/W4214656018
- DOI
- 10.1515/epoly-2022-0029
References
- https://openalex.org/W1836364420
- https://openalex.org/W1977072597
- https://openalex.org/W1999489116
- https://openalex.org/W2028424288
- https://openalex.org/W2040708261
- https://openalex.org/W2047925917
- https://openalex.org/W2048632096
- https://openalex.org/W2048854088
- https://openalex.org/W2057315210
- https://openalex.org/W2063110356
- https://openalex.org/W2072398283
- https://openalex.org/W2082516633
- https://openalex.org/W2084344211
- https://openalex.org/W2084572330
- https://openalex.org/W2092394037
- https://openalex.org/W2189978244
- https://openalex.org/W2417555774
- https://openalex.org/W2518955705
- https://openalex.org/W2561424020
- https://openalex.org/W2607462985
- https://openalex.org/W2616651209
- https://openalex.org/W2791538598
- https://openalex.org/W2804565634
- https://openalex.org/W2895245024
- https://openalex.org/W2898832795
- https://openalex.org/W2910493359
- https://openalex.org/W2947950474
- https://openalex.org/W2952105042
- https://openalex.org/W2966308492
- https://openalex.org/W2971740404
- https://openalex.org/W2999454106
- https://openalex.org/W3035671392
- https://openalex.org/W3094965000
- https://openalex.org/W3094969316
- https://openalex.org/W3114726241
- https://openalex.org/W3128611035
- https://openalex.org/W3164687926
- https://openalex.org/W3186645598
- https://openalex.org/W4248609371