Study of the Critical Behavior in La<sub>0.67</sub>Ca<sub>0.18</sub>Sr<sub>0.15</sub>Mn<sub>0.98</sub>Ni<sub>0.02</sub>O<sub>3</sub> Manganite Oxide

Creators

  • 1. University of Monastir

Description

In order to study the critical behavior of La0.67Ca0.18Sr0.15Mn0.98Ni0.02O3 near room temperature, magnetization measurements were performed. It can be seen from the findings that the specimens show a second order phase transition. Given the relative slope, the 3D-Ising model was deduced as the most suitable model. It was found that the evaluated critical exponents were β = 0.320, γ = 1.296 and δ = 4.965 at TC = 319 K. These verify the Broadom's scaling equation δ = 1 + γ/β, which demonstrates that our values have been proved valid. Near TC magnetization-strength-temperature, (M-μ0H-T) results fell in two curves according to critical exponents, obeying the single scaling equation Mμ0Hε=εβʄ±μ0H/εβ+γ with ε=T−Tc/Tc as the reduced temperature.

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

من أجل دراسة السلوك الحرج لـ La0.67Ca0.18Sr0.15Mn0.98Ni0.02O3 بالقرب من درجة حرارة الغرفة، تم إجراء قياسات المغنطة. يمكن أن نرى من النتائج أن العينات تظهر مرحلة انتقالية من الدرجة الثانية. بالنظر إلى المنحدر النسبي، تم استنتاج النموذج ثلاثي الأبعاد باعتباره النموذج الأنسب. وجد أن الأسس الحرجة التي تم تقييمها كانت β = 0.320 و γ = 1.296 و δ = 4.965 عند TC = 319 K. هذه تحقق من معادلة القياس في Broadom δ = 1 + γ/β، مما يدل على أن قيمنا قد ثبتت صحتها. بالقرب من درجة حرارة قوة مغنطة TC، انخفضت نتائج (M - μ 0 H - T) في منحنيين وفقًا للأسس الحرجة، مما أدى إلى اتباع معادلة القياس المفردة Mμ 0 Hε = εβ ± μ 0 H/εβ +γ مع ε=T−Tc/Tc كدرجة الحرارة المنخفضة.

Translated Description (French)

Afin d'étudier le comportement critique de La0,67Ca0,18Sr0,15Mn0,98Ni0,02O3 près de la température ambiante, des mesures de magnétisation ont été effectuées. Il ressort des résultats que les spécimens montrent une transition de phase du deuxième ordre. Compte tenu de la pente relative, le modèle 3D-Ising a été déduit comme le modèle le plus approprié. Il a été constaté que les exposants critiques évalués étaient β = 0,320, γ = 1,296 et δ = 4,965 à TC = 319 K. Ceux-ci vérifient l'équation d'échelle de Broadom δ = 1 + γ/β, ce qui démontre que nos valeurs ont été prouvées valides. Près de TC magnétisation-force-température, (M-μ0H-T) les résultats sont tombés dans deux courbes selon les exposants critiques, obéissant à l'équation de mise à l'échelle unique Mμ0Hε = εβ β ±μ0H/εβ+γ avec ε=T−Tc/Tc comme température réduite.

Translated Description (Spanish)

Para estudiar el comportamiento crítico de La0.67Ca0.18Sr0.15Mn0.98Ni0.02O3 cerca de la temperatura ambiente, se realizaron mediciones de magnetización. Se puede ver a partir de los hallazgos que las muestras muestran una transición de fase de segundo orden. Dada la pendiente relativa, el modelo 3D-Ising se dedujo como el modelo más adecuado. Se encontró que los exponentes críticos evaluados fueron β = 0.320, γ = 1.296 y δ = 4.965 en TC = 319 K. Estos verifican la ecuación de escala de Broadom δ = 1 + γ/β, lo que demuestra que nuestros valores han demostrado ser válidos. Cerca de TC magnetización-fuerza-temperatura, (M-μ0H-T) los resultados cayeron en dos curvas de acuerdo con los exponentes críticos, obedeciendo la ecuación de escala única Mμ0Hε = εβο ± μ0H/εβ+γ con ε=T−Tc/Tc como la temperatura reducida.

Files

81941.pdf

Files (1.7 MB)

⚠️ Please wait a few minutes before your translated files are ready ⚠️ Note: Some files might be protected thus translations might not work.
Name Size Download all
md5:e674365fcb25a4cfed856333d83376ec
1.7 MB
Preview Download

Additional details

Additional titles

Translated title (Arabic)
دراسة السلوك الحرج في LA<sub>0.67</sub>Ca<sub>0.18</sub>Sr<sub>0.15</sub>Mn<sub>0.98</sub>Ni<sub>0.02</sub>O<sub>3</sub> أكسيد المنغنيز
Translated title (French)
Etude du Comportement Critique en La<sub>0,67</sub>Ca<sub>0,18</sub>Sr<sub>0,15</sub>Mn<sub>0,98</sub>Ni<sub>0,02</sub>O<sub>3</sub> Oxyde de Manganite
Translated title (Spanish)
Estudio del Comportamiento Crítico en La<sub>0.67</sub>Ca<sub>0.18</sub>Sr<sub>0.15</sub>Mn<sub>0.98</sub>Ni<sub>0.02</sub>O<sub>3</sub> Óxido de Manganito

Identifiers

Other
https://openalex.org/W4285734767
DOI
10.5772/intechopen.105053

Is supplement to
https://openalex.org/W4390962471 (Other)
https://openalex.org/W3106283477 (Other)
https://openalex.org/W3127252294 (Other)
https://openalex.org/W2951852385 (Other)
https://openalex.org/W1598546354 (Other)
https://openalex.org/W2559080656 (Other)
https://openalex.org/W1963605683 (Other)
https://openalex.org/W1786270034 (Other)
https://openalex.org/W1975672403 (Other)
https://openalex.org/W2067021917 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Tunisia

References

  • https://openalex.org/W1605455207
  • https://openalex.org/W1615908694
  • https://openalex.org/W1967721615
  • https://openalex.org/W1971109699
  • https://openalex.org/W1980624489
  • https://openalex.org/W1985525739
  • https://openalex.org/W1986838699
  • https://openalex.org/W1992601919
  • https://openalex.org/W1998036731
  • https://openalex.org/W2013660200
  • https://openalex.org/W2024706737
  • https://openalex.org/W2030005132
  • https://openalex.org/W2030046989
  • https://openalex.org/W2042454844
  • https://openalex.org/W2056513692
  • https://openalex.org/W2059130734
  • https://openalex.org/W2075926292
  • https://openalex.org/W2088306357
  • https://openalex.org/W2142809461
  • https://openalex.org/W2751896937
  • https://openalex.org/W2769942661
  • https://openalex.org/W2803929056
  • https://openalex.org/W2808401579
  • https://openalex.org/W2947599136
  • https://openalex.org/W2962965393
  • https://openalex.org/W3047421695
  • https://openalex.org/W3099599107
  • https://openalex.org/W3105465697
  • https://openalex.org/W3181830337