Effect of recycled concrete powder on strength, electrical resistivity, and water absorption of self-compacting mortars

Creators

  • 1. Khon Kaen University

Description

The chemical composition of recycled concrete powder (RCP) and the physical properties of self-compacting mortar with RCP as supplementary cementitious materials (SCMs) were investigated in detail. RCP was obtained by crushing and sieving recycled concrete from demolished buildings; particles that passed No. 4 sieve (4.75 mm aperture) were then ground to a fineness such that 80% particles could pass through No. 325 sieve (45 µm aperture). The RCP partially replaced ordinary Portland cement (OPC) in varying ratios of 20%, 40%, and 60% by weight of powder in self-compacting mortars in which the water to powder ratio was maintained at 0.35. The compressive strength, electrical resistivity, porosity, and water absorption of the RCP self-compacting mortars were investigated. The results indicated that the RCP was reactive, having a strength-activity index of 89.4% and 87.2% at 7 and 28 days, respectively. The porosity and water absorption coefficient increased, and electrical resistivity decreased with an increase in the RCP content. Based on the results of this study, the optimum RCP replacement ratio with minimal negative effect on the compressive strength is up to 20%.

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

تم فحص التركيب الكيميائي لمسحوق الخرسانة المعاد تدويره (RCP) والخصائص الفيزيائية للملاط ذاتي الضغط مع RCP كمواد أسمنتية تكميلية (SCMs) بالتفصيل. تم الحصول على RCP عن طريق سحق وغربلة الخرسانة المعاد تدويرها من المباني المدمرة ؛ ثم تم طحن الجسيمات التي مرت بالمنخل رقم 4 (فتحة 4.75 مم) إلى درجة دقة بحيث يمكن أن تمر 80 ٪ من الجسيمات عبر المنخل رقم 325 (فتحة 45 ميكرومتر). حل RCP جزئيًا محل الأسمنت البورتلاندي العادي (OPC) بنسب متفاوتة تبلغ 20 ٪ و 40 ٪ و 60 ٪ بالوزن من المسحوق في الملاط ذاتي الضغط الذي تم فيه الحفاظ على نسبة الماء إلى المسحوق عند 0.35. تم فحص قوة الانضغاط والمقاومة الكهربائية والمسامية وامتصاص الماء لمدافع الهاون ذاتية الضغط RCP. أشارت النتائج إلى أن RCP كان تفاعليًا، حيث بلغ مؤشر نشاط القوة 89.4 ٪ و 87.2 ٪ في 7 و 28 يومًا على التوالي. زادت المسامية ومعامل امتصاص الماء، وانخفضت المقاومة الكهربائية مع زيادة محتوى RCP. استنادًا إلى نتائج هذه الدراسة، تصل نسبة استبدال RCP المثلى مع الحد الأدنى من التأثير السلبي على قوة الانضغاط إلى 20 ٪.

Translated Description (French)

La composition chimique de la poudre de béton recyclé (RCP) et les propriétés physiques du mortier autocompactant avec RCP comme matériaux cimentaires supplémentaires (SCM) ont été étudiées en détail. Le RCP a été obtenu par concassage et tamisage de béton recyclé provenant de bâtiments démolis ; les particules qui ont passé le tamis n ° 4 (ouverture de 4,75 mm) ont ensuite été broyées à une finesse telle que 80 % des particules ont pu passer à travers le tamis n ° 325 (ouverture de 45 µm). Le RCP a partiellement remplacé le ciment Portland ordinaire (OPC) dans des rapports variables de 20 %, 40 % et 60 % en poids de poudre dans des mortiers auto-compactants dans lesquels le rapport eau/poudre était maintenu à 0,35. La résistance à la compression, la résistivité électrique, la porosité et l'absorption d'eau des mortiers autocompactants RCP ont été étudiées. Les résultats ont indiqué que le RCP était réactif, ayant un indice de force-activité de 89,4% et 87,2% à 7 et 28 jours, respectivement. La porosité et le coefficient d'absorption d'eau ont augmenté, et la résistivité électrique a diminué avec une augmentation de la teneur en RCP. Sur la base des résultats de cette étude, le taux de remplacement optimal du RCP avec un effet négatif minimal sur la résistance à la compression peut atteindre 20 %.

Translated Description (Spanish)

Se investigó en detalle la composición química del polvo de concreto reciclado (RCP) y las propiedades físicas del mortero autocompactante con RCP como materiales cementosos suplementarios (SCM). El RCP se obtuvo triturando y tamizando concreto reciclado de edificios demolidos; las partículas que pasaron el tamiz No. 4 (abertura de 4.75 mm) se molieron a una finura tal que el 80% de las partículas pudieran pasar a través del tamiz No. 325 (abertura de 45 µm). El RCP reemplazó parcialmente al cemento Portland ordinario (OPC) en proporciones variables de 20%, 40% y 60% en peso de polvo en morteros autocompactantes en los que la proporción de agua a polvo se mantuvo en 0.35. Se investigó la resistencia a la compresión, la resistividad eléctrica, la porosidad y la absorción de agua de los morteros autocompactantes RCP. Los resultados indicaron que el RCP fue reactivo, teniendo un índice de fuerza-actividad de 89.4% y 87.2% a los 7 y 28 días, respectivamente. La porosidad y el coeficiente de absorción de agua aumentaron, y la resistividad eléctrica disminuyó con un aumento en el contenido de RCP. Con base en los resultados de este estudio, la relación óptima de reemplazo de RCP con un efecto negativo mínimo en la resistencia a la compresión es de hasta el 20%.

Additional details

Additional titles

Translated title (Arabic)
تأثير مسحوق الخرسانة المعاد تدويره على القوة والمقاومة الكهربائية وامتصاص الماء لمدافع الهاون ذاتية الضغط
Translated title (French)
Effet de la poudre de béton recyclé sur la résistance, la résistivité électrique et l'absorption d'eau des mortiers auto-compactants
Translated title (Spanish)
Efecto del polvo de hormigón reciclado sobre la resistencia, la resistividad eléctrica y la absorción de agua de los morteros autocompactantes

Identifiers

Other
https://openalex.org/W3203581460
DOI
10.1016/j.cscm.2021.e00725

Is supplement to
https://openalex.org/W4381376732 (Other)
https://openalex.org/W4238029295 (Other)
https://openalex.org/W4230350004 (Other)
https://openalex.org/W3011844621 (Other)
https://openalex.org/W2961776002 (Other)
https://openalex.org/W2317917829 (Other)
https://openalex.org/W2125466038 (Other)
https://openalex.org/W2057852806 (Other)
https://openalex.org/W2053178373 (Other)
https://openalex.org/W1537260658 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Thailand

References

  • https://openalex.org/W1994812940
  • https://openalex.org/W1995757921
  • https://openalex.org/W1997809384
  • https://openalex.org/W2000282519
  • https://openalex.org/W2007762754
  • https://openalex.org/W2043688602
  • https://openalex.org/W2047601566
  • https://openalex.org/W2056680342
  • https://openalex.org/W2075038045
  • https://openalex.org/W2077363979
  • https://openalex.org/W2077580407
  • https://openalex.org/W2082682529
  • https://openalex.org/W2088101126
  • https://openalex.org/W2107636689
  • https://openalex.org/W2136979141
  • https://openalex.org/W2570130824
  • https://openalex.org/W2620921585
  • https://openalex.org/W2626528381
  • https://openalex.org/W2747569630
  • https://openalex.org/W2801118399
  • https://openalex.org/W2903963044
  • https://openalex.org/W2942211170
  • https://openalex.org/W2990185176
  • https://openalex.org/W3092034230
  • https://openalex.org/W3127644349
  • https://openalex.org/W3137563030
  • https://openalex.org/W3154469442
  • https://openalex.org/W3172153045