Synthesis of trimetallic oxide (Fe2O3–MgO–CuO) nanocomposites and evaluation of their structural and optical properties

Creators

  • 1. Sana'a University
  • 2. Thamar University
  • 3. King Saud University

Description

Abstract In this paper, tri-phase Fe 2 O 3 –MgO–CuO nanocomposites (NCs) and pure CuO, Fe 2 O 3 and MgO nanoparticles (NPs) were prepared using sol–gel technique. The physical properties of the prepared products were examined using SEM, XRD, and UV–visible. The XRD data indicated the formation of pure CuO, Fe 2 O 3 and MgO NPs, as well as nanocomposite formation with Fe 2 O 3 (cubic), MgO (cubic), and CuO (monoclinic). The crystallite size of all the prepared samples was calculated via Scherrer's formula. The energy bandgap of CuO, Fe 2 O 3 and MgO and Fe 2 O 3 –MgO–CuO NCs were computed from UV–visible spectroscopy as following 2.13, 2.29, 5.43 and 2.96 eV, respectively. The results showed that Fe 2 O 3 –MgO–CuO NCs is an alternative material for a wide range of applications as optoelectronics devices due to their outstanding properties.

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

الملخص في هذه الورقة، تم تحضير المركبات النانوية ثلاثية الطور Fe 2 O 3 - MgO - CuO (NCs) و CuO النقي و Fe 2 O 3 والجسيمات النانوية MgO (NPs) باستخدام تقنية Sol - gel. تم فحص الخصائص الفيزيائية للمنتجات المحضرة باستخدام SEM و XRD و UV - visible. أشارت بيانات XRD إلى تكوين CuO النقي و Fe 2 O 3 و MgO NPs، بالإضافة إلى تكوين المركبات النانوية مع Fe 2 O 3 (مكعب) و MgO (مكعب) و CuO (أحادي الميل). تم حساب حجم البلورات لجميع العينات المحضرة من خلال صيغة شيرر. تم حساب فجوة نطاق الطاقة لـ CuO و Fe 2 O 3 و MgO و Fe 2 O 3 - MgO - CuO NCs من التحليل الطيفي المرئي للأشعة فوق البنفسجية على النحو التالي 2.13 و 2.29 و 5.43 و 2.96 eV، على التوالي. أظهرت النتائج أن الحديد 2 O 3 - MgO - CuO NCs هو مادة بديلة لمجموعة واسعة من التطبيقات كأجهزة الإلكترونيات الضوئية بسبب خصائصها المتميزة.

Translated Description (French)

Résumé Dans cet article, des nanocomposites triphasés Fe 2 O 3 –MgO–CuO (NCs) et des nanoparticules de CuO, Fe 2 O 3 et MgO (NPs) pures ont été préparés en utilisant la technique sol–gel. Les propriétés physiques des produits préparés ont été examinées à l'aide de MEB, DRX et UV–visible. Les données XRD ont indiqué la formation de NP de CuO, Fe 2 O 3 et MgO purs, ainsi que la formation de nanocomposites avec Fe 2 O 3 (cubique), MgO (cubique) et CuO (monoclinique). La taille des cristallites de tous les échantillons préparés a été calculée à l'aide de la formule de Scherrer. La bande interdite d'énergie des NC CuO, Fe 2 O 3 et MgO et Fe 2 O 3 –MgO–CuO a été calculée à partir de la spectroscopie UV–visible comme suit 2,13, 2,29, 5,43 et 2,96 eV, respectivement. Les résultats ont montré que les NC Fe 2 O 3 -MgO-CuO sont un matériau alternatif pour un large éventail d'applications en tant que dispositifs optoélectroniques en raison de leurs propriétés exceptionnelles.

Translated Description (Spanish)

Resumen En este artículo, se prepararon nanocompuestos (NC) trifásicos de Fe2O3-MgO-CuO y nanopartículas (NP) puras de CuO, Fe2O3 y MgO utilizando la técnica sol–gel. Las propiedades físicas de los productos preparados se examinaron utilizando SEM, XRD y UV–visible. Los datos de XRD indicaron la formación de CuO puro, Fe 2 O 3 y MgO NP, así como la formación de nanocompuestos con Fe 2 O 3 (cúbico), MgO (cúbico) y CuO (monoclínico). El tamaño de los cristalitos de todas las muestras preparadas se calculó mediante la fórmula de Scherrer. La brecha de banda de energía de CuO, Fe 2 O 3 y MgO y Fe 2 O 3 –MgO–CuO NC se calcularon a partir de espectroscopía UV–visible de la siguiente manera 2.13, 2.29, 5.43 y 2.96 eV, respectivamente. Los resultados mostraron que los NC de Fe 2 O 3 -MgO-CuO son un material alternativo para una amplia gama de aplicaciones como dispositivos optoelectrónicos debido a sus propiedades sobresalientes.

Files

s41598-023-39845-5.pdf.pdf

Files (1.9 MB)

⚠️ Please wait a few minutes before your translated files are ready ⚠️ Note: Some files might be protected thus translations might not work.
Name Size Download all
md5:af616628bbd1ecc79bb6e75993aa7189
1.9 MB
Preview Download

Additional details

Additional titles

Translated title (Arabic)
تركيب المركبات النانوية للأكسيد الثلاثي الفلزات (Fe2O3 - mgO - CuO) وتقييم خصائصها الهيكلية والبصرية
Translated title (French)
Synthèse des nanocomposites d'oxyde trimétallique (Fe2O3-MgO-CuO) et évaluation de leurs propriétés structurales et optiques
Translated title (Spanish)
Síntesis de nanocompuestos de óxido trimetálico (Fe2O3-MgO-CuO) y evaluación de sus propiedades estructurales y ópticas

Identifiers

Other
https://openalex.org/W4385693726
DOI
10.1038/s41598-023-39845-5

Is supplement to
https://openalex.org/W2320118746 (Other)
https://openalex.org/W1964159414 (Other)
https://openalex.org/W2010011859 (Other)
https://openalex.org/W3215954879 (Other)
https://openalex.org/W2086299624 (Other)
https://openalex.org/W1981634121 (Other)
https://openalex.org/W3098378679 (Other)
https://openalex.org/W2107898007 (Other)
https://openalex.org/W2101143665 (Other)
https://openalex.org/W2804141023 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Yemen

References

  • https://openalex.org/W284881392
  • https://openalex.org/W1976211764
  • https://openalex.org/W2010800706
  • https://openalex.org/W2253724643
  • https://openalex.org/W2557289526
  • https://openalex.org/W2767781151
  • https://openalex.org/W2768073181
  • https://openalex.org/W2799749586
  • https://openalex.org/W2891983715
  • https://openalex.org/W2897749064
  • https://openalex.org/W2912827791
  • https://openalex.org/W2913924637
  • https://openalex.org/W2914076352
  • https://openalex.org/W2944253162
  • https://openalex.org/W2975362071
  • https://openalex.org/W2989714303
  • https://openalex.org/W3009884108
  • https://openalex.org/W3023736553
  • https://openalex.org/W3025262880
  • https://openalex.org/W3033933264
  • https://openalex.org/W3044319595
  • https://openalex.org/W3096547696
  • https://openalex.org/W3110784363
  • https://openalex.org/W3113118933
  • https://openalex.org/W3127511274
  • https://openalex.org/W3147714106
  • https://openalex.org/W3168739051
  • https://openalex.org/W4205563833
  • https://openalex.org/W4220869830
  • https://openalex.org/W4283275047
  • https://openalex.org/W4283318254
  • https://openalex.org/W4291993813
  • https://openalex.org/W4292722409
  • https://openalex.org/W4297908074
  • https://openalex.org/W4315781899
  • https://openalex.org/W4320182161
  • https://openalex.org/W4323047459
  • https://openalex.org/W4381803351
  • https://openalex.org/W4385693726