Fabrication of Ag@Co-Al Layered Double Hydroxides Reinforced poly(o-phenylenediamine) Nanohybrid for Efficient Electrochemical Detection of 4-Nitrophenol, 2,4-Dinitrophenol and Uric acid at Nano Molar Level
Creators
- 1. University of Madras
- 2. University of Electronic Science and Technology of China
- 3. University of Concepción
- 4. Central Electrochemical Research Institute
Description
In this paper, Co-Al layered double hydroxides (LDHs), Co-Al LDHs/poly(o-phenylenediamine) (PoPD) and Ag nanoparticles decorated Co-Al LDHs/PoPD (Ag@Co-Al LDH/PoPD) samples were prepared. The as-prepared samples were characterized by XRD, Raman, XPS, FT-IR, DRS-UV-Vis, PL and TGA techniques. The salient features of morphology and size of the samples were determined using FESEM, and HR-TEM. Then, the samples were coated on glassy carbon electrode (GCE) and employed for sensing of 4-nitrophenol (4-NP), 2,4-dinitrophenol (2,4-DNP)) and uric acid (UA). It was found that Ag@Co-Al LDH/PoPD/GCE showed superior electrochemical sensing behaviour than other modified electrodes. It exhibits the detection limit (DL) of 63 nM, 50 nM and 0.28 µM for 4-NP, 2,4-DNP and UA respectively.
Translated Descriptions
⚠️
This is an automatic machine translation with an accuracy of 90-95%
Translated Description (Arabic)
في هذه الورقة، تم إعداد عينات من الهيدروكسيدات المزدوجة ذات الطبقات المشتركة (LDHs)، و LDHs/POLY (o - phenylenediamine) (PoPD) و Ag nanoparticles المزينة بـ Co - Al LDHs/PoPD (Ag@ Co - Al LDH/PoPD). تميزت العينات المعدة بتقنيات XRD و Raman و XPS و FT - IR و DRS - UV - Vis و PL و TGA. تم تحديد السمات البارزة للمورفولوجيا وحجم العينات باستخدام FESEM و HR - TEM. بعد ذلك، تم طلاء العينات على قطب الكربون الزجاجي (GCE) واستخدمت لاستشعار 4 -نيتروفينول (4 - NP)، 2،4 -دينيتروفينول (2،4 - DNP)) وحمض اليوريك (UA). تبين أن Ag@ Co - Al LDH/PoPD/GCE أظهرت سلوك استشعار كهروكيميائي متفوق على الأقطاب الكهربائية المعدلة الأخرى. يُظهر حد الكشف (DL) البالغ 63 نانومتر و 50 نانومتر و 0.28 ميكرومتر لـ 4 - NP و 2،4 - DNP و UA على التوالي.Translated Description (French)
Dans cet article, des échantillons d'hydroxydes doubles en couches Co-Al (LDH), de LDH Co-Al/poly(o-phénylènediamine) (PoPD) et de nanoparticules d'Ag décorées de LDH Co-Al/PoPD (Ag@Co-Al LDH/PoPD) ont été préparés. Les échantillons tels que préparés ont été caractérisés par les techniques DRX, Raman, XPS, FT-IR, DRS-UV-Vis, PL et TGA. Les caractéristiques saillantes de la morphologie et de la taille des échantillons ont été déterminées à l'aide de FESEM et de HR-TEM. Ensuite, les échantillons ont été revêtus sur une électrode de carbone vitreux (GCE) et utilisés pour détecter le 4-nitrophénol (4-NP), le 2,4-dinitrophénol (2,4-DNP)) et l'acide urique (UA). Il a été constaté que Ag@Co-Al LDH/PoPD/GCE présentait un comportement de détection électrochimique supérieur à celui des autres électrodes modifiées. Il présente la limite de détection (DL) de 63 nM, 50 nM et 0,28 µM pour le 4-NP, le 2,4-DNP et l'UA respectivement.Translated Description (Spanish)
En este documento, se prepararon muestras de hidróxidos dobles en capas de Co-Al (LDH), Co-Al LDH/poli(o-fenilendiamina) (PoPD) y nanopartículas de Ag decoradas con Co-Al LDH/PoPD (Ag@Co-Al LDH/PoPD). Las muestras preparadas se caracterizaron mediante técnicas XRD, Raman, XPS, FT-IR, DRS-UV-Vis, PL y TGA. Las características sobresalientes de la morfología y el tamaño de las muestras se determinaron utilizando FESEM y HR-TEM. Luego, las muestras se recubrieron con un electrodo de carbono vítreo (GCE) y se emplearon para detectar 4-nitrofenol (4-NP), 2,4-dinitrofenol (2,4-DNP)) y ácido úrico (UA). Se encontró que Ag@Co-Al LDH/PoPD/GCE mostró un comportamiento de detección electroquímica superior que otros electrodos modificados. Presenta el límite de detección (DL) de 63 nM, 50 nM y 0.28 µM para 4-NP, 2,4-DNP y UA respectivamente.Files
s41598-019-49595-y.pdf.pdf
Files
(3.9 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:5f8b63bb641c88d942ef74f2a81bd902
|
3.9 MB | Preview Download |
Additional details
Additional titles
- Translated title (Arabic)
- تصنيع مركبات الهيدروكسيد المزدوجة ذات الطبقات المعززة من البولي(o - phenylenediamine) الهجين النانوي للكشف الكهروكيميائي الفعال عن 4 -نيتروفينول و 2،4 -دينتروفينول وحمض اليوريك على مستوى النانو المولاري
- Translated title (French)
- Fabrication de poly(o-phénylènediamine) nanohybride renforcé d'hydroxydes doubles en couches Ag@Co-Al pour une détection électrochimique efficace du 4-nitrophénol, du 2,4-dinitrophénol et de l'acide urique au niveau nanométrique
- Translated title (Spanish)
- Fabricación de nanohíbrido de poli(o-fenilendiamina) reforzado con hidróxidos dobles de Ag@Co-Al para la detección electroquímica eficiente de 4-nitrofenol, 2,4-dinitrofenol y ácido úrico a nivel nanomolar
Identifiers
- Other
- https://openalex.org/W2972642075
- DOI
- 10.1038/s41598-019-49595-y
References
- https://openalex.org/W1965269594
- https://openalex.org/W1974665748
- https://openalex.org/W1976456910
- https://openalex.org/W1979575075
- https://openalex.org/W1979793695
- https://openalex.org/W1980653653
- https://openalex.org/W1991053649
- https://openalex.org/W1994956453
- https://openalex.org/W1995565591
- https://openalex.org/W2003648205
- https://openalex.org/W2006636051
- https://openalex.org/W2015090931
- https://openalex.org/W2017166307
- https://openalex.org/W2020873169
- https://openalex.org/W2022985354
- https://openalex.org/W2030724819
- https://openalex.org/W2033103345
- https://openalex.org/W2038956587
- https://openalex.org/W2049098205
- https://openalex.org/W2054694765
- https://openalex.org/W2057093756
- https://openalex.org/W2060715248
- https://openalex.org/W2061994972
- https://openalex.org/W2062563245
- https://openalex.org/W2070044219
- https://openalex.org/W2075794631
- https://openalex.org/W2081535591
- https://openalex.org/W2083595698
- https://openalex.org/W2088246810
- https://openalex.org/W2090045801
- https://openalex.org/W2106979537
- https://openalex.org/W2194103875
- https://openalex.org/W2259909106
- https://openalex.org/W2288925909
- https://openalex.org/W2323170603
- https://openalex.org/W2470143562
- https://openalex.org/W2483054846
- https://openalex.org/W2537807713
- https://openalex.org/W2555083661
- https://openalex.org/W2572633859
- https://openalex.org/W2574619931
- https://openalex.org/W2601118772
- https://openalex.org/W2736791360
- https://openalex.org/W2750629309
- https://openalex.org/W2772499517
- https://openalex.org/W2773007283
- https://openalex.org/W2781399048
- https://openalex.org/W2792708005
- https://openalex.org/W2799507535
- https://openalex.org/W2800643155
- https://openalex.org/W2801023552
- https://openalex.org/W2806639400
- https://openalex.org/W2892684050