Preparation and Characterization of Mixed-Oxide Catalyst
Creators
- 1. Sokoto State University
- 2. Usmanu Danfodiyo University
Description
Solid heterogeneous CuO-MoO3/ZrO2 catalyst was prepared by impregnation using suitable precursor materials supported over zirconia. Upon calcination at 450°C for 2 hours, available techniques were employed for the characterization. The available oxides and minerals in the catalyst were revealed by the XRF and XRD profiles respectively. The catalyst crystallite size (131.6nm) was obtained using the Bragg's equation from the latter. Thermal analysis showed three weight loss stages between (49.25-152.06°C), (152.06-559.47°C) and (559.47-752.0°C) while presence of sulphate and zirconia oxides was revealed by the FTIR analysis due to appearance of absorption bands around 1225-980cm-1 and 700-600 cm-1 respectively.
Translated Descriptions
⚠️
This is an automatic machine translation with an accuracy of 90-95%
Translated Description (Arabic)
تم تحضير محفز CuO - MoO3/ZrO2 الصلب غير المتجانس عن طريق التشريب باستخدام مواد سليفة مناسبة مدعومة فوق الزركونيا. عند التكليس عند 450 درجة مئوية لمدة ساعتين، تم استخدام التقنيات المتاحة للتوصيف. تم الكشف عن الأكاسيد والمعادن المتاحة في المحفز من خلال ملفات تعريف XRF و XRD على التوالي. تم الحصول على حجم بلورات المحفز (131.6 نانومتر) باستخدام معادلة براغ من الأخير. أظهر التحليل الحراري ثلاث مراحل لفقدان الوزن بين (49.25-152.06 درجة مئوية) و (152.06-559.47 درجة مئوية) و (559.47-752.0 درجة مئوية) بينما تم الكشف عن وجود أكاسيد الكبريتات والزركونيا من خلال تحليل FTIR بسبب ظهور نطاقات الامتصاص حول 1225-980 سم -1 و 700-600 سم -1 على التوالي.Translated Description (French)
Le catalyseur solide hétérogène CuO-MoO3/ZrO2 a été préparé par imprégnation à l'aide de matériaux précurseurs appropriés supportés sur de la zircone. Après calcination à 450°C pendant 2 heures, les techniques disponibles ont été utilisées pour la caractérisation. Les oxydes et minéraux disponibles dans le catalyseur ont été révélés par les profils XRF et XRD respectivement. La taille des cristallites du catalyseur (131,6 nm) a été obtenue en utilisant l'équation de Bragg à partir de cette dernière. L'analyse thermique a montré trois stades de perte de poids entre (49,25-152,06°C), (152,06-559,47°C) et (559,47-752,0°C) tandis que la présence d'oxydes de sulfate et de zircone a été révélée par l'analyse IRTF en raison de l'apparition de bandes d'absorption autour de 1225-980cm-1 et 700-600 cm-1 respectivement.Translated Description (Spanish)
El catalizador sólido heterogéneo de CuO-MoO3/ZrO2 se preparó mediante impregnación utilizando materiales precursores adecuados soportados sobre zirconia. Tras la calcinación a 450 °C durante 2 horas, se emplearon técnicas disponibles para la caracterización. Los óxidos y minerales disponibles en el catalizador fueron revelados por los perfiles XRF y XRD respectivamente. El tamaño del cristalito del catalizador (131,6 nm) se obtuvo utilizando la ecuación de Bragg de este último. El análisis térmico mostró tres etapas de pérdida de peso entre (49.25-152.06°C), (152.06-559.47°C) y (559.47-752.0°C), mientras que la presencia de óxidos de sulfato y circonio se reveló mediante el análisis FTIR debido a la aparición de bandas de absorción alrededor de 1225-980cm-1 y 700-600 cm-1 respectivamente.Files
101.pdf
Files
(188.9 kB)
| Name | Size | Download all |
|---|---|---|
|
md5:90ca9e6de972895c886f83f3bf29df35
|
188.9 kB | Preview Download |
Additional details
Additional titles
- Translated title (Arabic)
- تحضير وتوصيف محفز الأكسيد المختلط
- Translated title (French)
- Préparation et caractérisation du catalyseur à oxydes mixtes
- Translated title (Spanish)
- Preparación y caracterización del catalizador de óxido mixto
Identifiers
- Other
- https://openalex.org/W2980709730
- DOI
- 10.34198/ejcs.2219.293302
References
- https://openalex.org/W1977833019
- https://openalex.org/W1990383084
- https://openalex.org/W2049037747
- https://openalex.org/W2052539398
- https://openalex.org/W2056664162
- https://openalex.org/W2060485349
- https://openalex.org/W2069419818
- https://openalex.org/W2074762780
- https://openalex.org/W2096503162
- https://openalex.org/W2117748396
- https://openalex.org/W2293783715
- https://openalex.org/W2620071387