Surface Mo or Ni-Enrichment Applied to Granulated Self-Lubricating Composites: Microstructural and Tribological Evaluation

Creators

  • 1. Instituto Federal de Educação, Ciência e Tecnologia de Santa Catarina
  • 2. Universidade Federal de Santa Catarina
  • 3. Universidade Federal de Uberlândia

Description

Sintered self-lubricating components may present inappropriate mechanical properties despite their excellent tribological properties. In general, alloying elements are used to improve these properties, but with a cost increase. As an alternative, surface enrichment (or surface alloying) with alloying elements may be applied. This study developed and characterized sintered composite materials surface-enriched with nickel or molybdenum. The results showed that the surface enrichment process is useful for increasing the tribomechanical properties. The Mo-enriched samples presented superior tribological results. Compared with the reference samples (not enriched), the Mo-enriched specimens showed an increase of 4,954% in scuffing resistance, lower friction coefficient (0.09), and reduced wear rate (68% and 96% lower for the specimen and the counter body). These results were mainly attributed to microstructural modification.

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

قد تظهر مكونات التشحيم الذاتي الملبدة خصائص ميكانيكية غير مناسبة على الرغم من خصائصها الثلاثية الممتازة. بشكل عام، يتم استخدام عناصر السبائك لتحسين هذه الخصائص، ولكن مع زيادة التكلفة. كبديل، يمكن استخدام التخصيب السطحي (أو السبائك السطحية) مع عناصر السبائك. طورت هذه الدراسة وسمت المواد المركبة الملبدة المخصبة بالنيكل أو الموليبدينوم. أظهرت النتائج أن عملية التخصيب السطحي مفيدة لزيادة الخواص الميكانيكية الثلاثية. قدمت العينات المخصبة نتائج قبليّة متفوقة. بالمقارنة مع العينات المرجعية (غير المخصبة)، أظهرت العينات المخصبة مو زيادة بنسبة 4،954 ٪ في مقاومة الاحتكاك، وانخفاض معامل الاحتكاك (0.09)، وانخفاض معدل التآكل (68 ٪ و 96 ٪ أقل للعينة والجسم المضاد). تُعزى هذه النتائج بشكل أساسي إلى التعديل الهيكلي الدقيق.

Translated Description (French)

Les composants autolubrifiants frittés peuvent présenter des propriétés mécaniques inappropriées malgré leurs excellentes propriétés tribologiques. En général, les éléments d'alliage sont utilisés pour améliorer ces propriétés, mais avec une augmentation des coûts. En variante, un enrichissement de surface (ou un alliage de surface) avec des éléments d'alliage peut être appliqué. Cette étude a développé et caractérisé des matériaux composites frittés enrichis en surface avec du nickel ou du molybdène. Les résultats ont montré que le processus d'enrichissement de surface est utile pour augmenter les propriétés tribomécaniques. Les échantillons enrichis en Mo présentaient des résultats tribologiques supérieurs. Par rapport aux échantillons de référence (non enrichis), les échantillons enrichis en Mo ont montré une augmentation de 4 954 % de la résistance aux éraflures, un coefficient de frottement plus faible (0,09) et un taux d'usure réduit (68 % et 96 % plus bas pour l'échantillon et le contre-corps). Ces résultats ont été principalement attribués à la modification microstructurale.

Translated Description (Spanish)

Los componentes autolubricantes sinterizados pueden presentar propiedades mecánicas inapropiadas a pesar de sus excelentes propiedades tribológicas. En general, los elementos de aleación se utilizan para mejorar estas propiedades, pero con un aumento de los costes. Como alternativa, se puede aplicar enriquecimiento superficial (o aleación superficial) con elementos de aleación. Este estudio desarrolló y caracterizó materiales compuestos sinterizados enriquecidos superficialmente con níquel o molibdeno. Los resultados mostraron que el proceso de enriquecimiento superficial es útil para aumentar las propiedades tribomecánicas. Las muestras enriquecidas con Mo presentaron resultados tribológicos superiores. En comparación con las muestras de referencia (no enriquecidas), las muestras enriquecidas con Mo mostraron un aumento del 4,954% en la resistencia al rayado, un coeficiente de fricción más bajo (0.09) y una tasa de desgaste reducida (68% y 96% más baja para la muestra y el cuerpo del contador). Estos resultados se atribuyeron principalmente a la modificación microestructural.

Files

pdf.pdf

Files (3.0 MB)

⚠️ Please wait a few minutes before your translated files are ready ⚠️ Note: Some files might be protected thus translations might not work.
Name Size Download all
md5:d4bfcad087a923ea5cb18fa75f1e7e55
3.0 MB
Preview Download

Additional details

Additional titles

Translated title (Arabic)
التركيب السطحي أو الإثراء بالنيكل المطبق على مركبات التشحيم الذاتي الحبيبية: التقييم البنيوي الدقيق والتقييم القبلي
Translated title (French)
Surface Mo ou Ni-Enrichissement Appliqué aux Composites Autolubrifiants Granulés : Évaluation Microstructurale et Tribologique
Translated title (Spanish)
Superficie de Mo o enriquecimiento de Ni aplicado a compuestos autolubricantes granulados: evaluación microestructural y tribológica

Identifiers

Other
https://openalex.org/W4282974489
DOI
10.3389/fmech.2022.921826

Is supplement to
https://openalex.org/W3143908150 (Other)
https://openalex.org/W2800119364 (Other)
https://openalex.org/W2792156184 (Other)
https://openalex.org/W2784235361 (Other)
https://openalex.org/W2741269701 (Other)
https://openalex.org/W2358069765 (Other)
https://openalex.org/W2308701346 (Other)
https://openalex.org/W2060526068 (Other)
https://openalex.org/W2009434284 (Other)
https://openalex.org/W1980845478 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Brazil

References

  • https://openalex.org/W1480382056
  • https://openalex.org/W1534385194
  • https://openalex.org/W1650538669
  • https://openalex.org/W1695406099
  • https://openalex.org/W1925496554
  • https://openalex.org/W1967615955
  • https://openalex.org/W1984525872
  • https://openalex.org/W1993214558
  • https://openalex.org/W1998352487
  • https://openalex.org/W2000066578
  • https://openalex.org/W2004592469
  • https://openalex.org/W2009272631
  • https://openalex.org/W2015191299
  • https://openalex.org/W2019984268
  • https://openalex.org/W2029184265
  • https://openalex.org/W2033043132
  • https://openalex.org/W2052547189
  • https://openalex.org/W2054182874
  • https://openalex.org/W2061612061
  • https://openalex.org/W2069356471
  • https://openalex.org/W2076527530
  • https://openalex.org/W2082076578
  • https://openalex.org/W2087399354
  • https://openalex.org/W2089786627
  • https://openalex.org/W2093249850
  • https://openalex.org/W2093874420
  • https://openalex.org/W2120319371
  • https://openalex.org/W2123125078
  • https://openalex.org/W2152957017
  • https://openalex.org/W2165166563
  • https://openalex.org/W2171635403
  • https://openalex.org/W2183813247
  • https://openalex.org/W233633408
  • https://openalex.org/W2405817265
  • https://openalex.org/W2475944651
  • https://openalex.org/W2508003026
  • https://openalex.org/W2547297107
  • https://openalex.org/W2560644047
  • https://openalex.org/W2625689411
  • https://openalex.org/W2725754503
  • https://openalex.org/W2750857672
  • https://openalex.org/W2752721916
  • https://openalex.org/W2780946118
  • https://openalex.org/W2806314905
  • https://openalex.org/W2895842296
  • https://openalex.org/W2923658402
  • https://openalex.org/W2939935764
  • https://openalex.org/W2983404349
  • https://openalex.org/W3009538839
  • https://openalex.org/W3022995300
  • https://openalex.org/W4377938662
  • https://openalex.org/W597755682
  • https://openalex.org/W641289383