<b>Basalt waste added to Portland cement
- 1. Universidade Tecnológica Federal do Paraná
- 2. Universidade Estadual de Londrina
Description
Portland cement is widely used as a building material and more than 4.3 billion tons were produced in 2014, with increasing environmental impacts by this industry, mainly through CO2 emissions and consumption of non-removable raw materials. Several by-products have been used as raw materials or fuels to reduce environmental impacts. Basaltic waste collected by filters was employed as a mineral mixture to Portland cement and two fractions were tested. The compression strength of mortars was measured after 7 days and Scanning Electron Microscopy (SEM) and Electron Diffraction Scattering (EDS) were carried out on Portland cement paste with the basaltic residue. Gains in compression strength were observed for mixtures containing 2.5 wt.% of basaltic residue. Hydration products observed on surface of basaltic particles show the nucleation effect of mineral mixtures. Clinker substitution by mineral mixtures reduces CO2 emission per ton of Portland cement.
Translated Descriptions
⚠️
This is an automatic machine translation with an accuracy of 90-95%
Translated Description (Arabic)
يستخدم الأسمنت البورتلاندي على نطاق واسع كمواد بناء وتم إنتاج أكثر من 4.3 مليار طن في عام 2014، مع زيادة الآثار البيئية لهذه الصناعة، وذلك بشكل رئيسي من خلال انبعاثات ثاني أكسيد الكربون واستهلاك المواد الخام غير القابلة للإزالة. تم استخدام العديد من المنتجات الثانوية كمواد خام أو وقود للحد من الآثار البيئية. تم استخدام النفايات البازلتية التي تم جمعها بواسطة المرشحات كخليط معدني للأسمنت البورتلاندي وتم اختبار جزأين. تم قياس قوة انضغاط الملاط بعد 7 أيام وتم إجراء الفحص المجهري الإلكتروني (SEM) وتشتت حيود الإلكترون (EDS) على معجون الأسمنت البورتلاندي مع البقايا البازلتية. لوحظت مكاسب في قوة الانضغاط للمخاليط التي تحتوي على 2.5 ٪ بالوزن من بقايا البازلت. تُظهر منتجات الترطيب التي لوحظت على سطح الجسيمات البازلتية تأثير التنوي للخلائط المعدنية. يقلل استبدال الكلنكر بالمخاليط المعدنية من انبعاثات ثاني أكسيد الكربون لكل طن من الأسمنت البورتلاندي.Translated Description (French)
Le ciment Portland est largement utilisé comme matériau de construction et plus de 4,3 milliards de tonnes ont été produites en 2014, avec des impacts environnementaux croissants de cette industrie, principalement à travers les émissions de CO2 et la consommation de matières premières non amovibles. Plusieurs sous-produits ont été utilisés comme matières premières ou combustibles pour réduire les impacts environnementaux. Les déchets basaltiques collectés par les filtres ont été utilisés comme mélange minéral pour le ciment Portland et deux fractions ont été testées. La résistance à la compression des mortiers a été mesurée après 7 jours et la microscopie électronique à balayage (MEB) et la diffusion par diffraction électronique (EDS) ont été effectuées sur la pâte de ciment Portland avec le résidu basaltique. Des gains de résistance à la compression ont été observés pour les mélanges contenant 2,5 % en poids de résidu basaltique. Les produits d'hydratation observés à la surface des particules basaltiques montrent l'effet de nucléation des mélanges minéraux. Le remplacement du clinker par des mélanges minéraux réduit les émissions de CO2 par tonne de ciment Portland.Translated Description (Spanish)
El cemento portland es ampliamente utilizado como material de construcción y en 2014 se produjeron más de 4.300 millones de toneladas, con impactos ambientales cada vez mayores por parte de esta industria, principalmente a través de las emisiones de CO2 y el consumo de materias primas no extraíbles. Se han utilizado varios subproductos como materias primas o combustibles para reducir los impactos ambientales. Los residuos basálticos recogidos por los filtros se emplearon como una mezcla mineral para el cemento Portland y se probaron dos fracciones. La resistencia a la compresión de los morteros se midió después de 7 días y la microscopía electrónica de barrido (SEM) y la dispersión por difracción de electrones (EDS) se llevaron a cabo en pasta de cemento Portland con el residuo basáltico. Se observaron ganancias en la resistencia a la compresión para mezclas que contenían 2.5% en peso de residuo basáltico. Los productos de hidratación observados en la superficie de las partículas basálticas muestran el efecto de nucleación de las mezclas minerales. La sustitución de clínker por mezclas minerales reduce la emisión de CO2 por tonelada de cemento Portland.Files
pdf.pdf
Files
(257 Bytes)
| Name | Size | Download all |
|---|---|---|
|
md5:af092f95a40a5ffd63d047426412a523
|
257 Bytes | Preview Download |
Additional details
Additional titles
- Translated title (Arabic)
- <b> نفايات البازلت المضافة إلى الأسمنت البورتلاندي
- Translated title (French)
- <b> Déchets de basalte ajoutés au ciment Portland
- Translated title (Spanish)
- <b> Residuos de basalto añadidos al cemento Portland
Identifiers
- Other
- https://openalex.org/W2514015148
- DOI
- 10.4025/actascitechnol.v38i4.27290
References
- https://openalex.org/W1950275058
- https://openalex.org/W1965672905
- https://openalex.org/W1971931931
- https://openalex.org/W1988699382
- https://openalex.org/W1997354286
- https://openalex.org/W1999485019
- https://openalex.org/W2016363807
- https://openalex.org/W2022460742
- https://openalex.org/W2037038536
- https://openalex.org/W2066642729
- https://openalex.org/W2067243794
- https://openalex.org/W2074868008
- https://openalex.org/W2077546874
- https://openalex.org/W2079100964
- https://openalex.org/W2079921540
- https://openalex.org/W2102852875
- https://openalex.org/W2118682646
- https://openalex.org/W2125151706
- https://openalex.org/W2142560767
- https://openalex.org/W226929994
- https://openalex.org/W2443612639
- https://openalex.org/W2950888313