Chemical Changes Associated with Increased Acid Resistance of Er:YAG Laser Irradiated Enamel

Creators

  • 1. Universidad Autónoma del Estado de México
  • 2. Universidad Nacional Autónoma de México

Description

An increase in the acid resistance of dental enamel, as well as morphological and structural changes produced by Er:YAG laser irradiation, has been reported.To evaluate the chemical changes associated with acid resistance of enamel treated with Er:YAG laser. Methods. Forty-eight enamel samples were divided into 4 groups (n = 12). Group I (control); Groups II, III, and IV were irradiated with Er:YAG at 100 mJ (12.7 J/cm(2)), 200 mJ (25.5 J/cm(2)), and 300 mJ (38.2 J/cm(2)), respectively.There were significant differences in composition of irradiated groups (with the exception of chlorine) and in the amount of calcium released.Chemical changes associated with an increase in acid resistance of enamel treated with Er:YAG laser showed a clear postirradiation pattern characterized by a decrease in C at.% and an increase in O, P, and Ca at.% and no changes in Cl at.%. An increased Ca/P ratio after Er:YAG laser irradiation was associated with the use of higher laser energy densities. Chemical changes produced by acid dissolution showed a similar trend among experimental groups. Stable or increased Ca/P ratio after acid dissolution was observed in the irradiated groups, with reduction of Ca released into the acid solution.

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

تم الإبلاغ عن زيادة في المقاومة الحمضية لمينا الأسنان، بالإضافة إلى التغيرات الشكلية والهيكلية التي تنتجها أشعة الليزر Er:YAG. لتقييم التغيرات الكيميائية المرتبطة بمقاومة الحمض للمينا المعالجة باستخدام ليزر Er:YAG. الطرق. تم تقسيم ثمانية وأربعين عينة من المينا إلى 4 مجموعات (العدد = 12). المجموعة الأولى (التحكم) ؛ تم تشعيع المجموعات الثانية والثالثة والرابعة بـ Er:YAG عند 100 مللي جول (12.7 جول/سم(2))، 200 مللي جول (25.5 جول/سم(2))، و 300 مللي جول (38.2 جول/سم(2))، على التوالي. كانت هناك اختلافات كبيرة في تكوين المجموعات المشعة (باستثناء الكلور) وفي كمية الكالسيوم المنبعثة. أظهرت التغيرات الكيميائية المرتبطة بزيادة المقاومة الحمضية للمينا المعالجة بـ Er:YAG laser نمطًا واضحًا للإشعاع اللاحق يتميز بانخفاض في C عند.٪ وزيادة في O و P و Ca عند.٪ ولا توجد تغييرات في Cl عند.٪. ارتبطت زيادة نسبة Ca/P بعد تشعيع ليزر Er:YAG باستخدام كثافة طاقة ليزر أعلى. أظهرت التغيرات الكيميائية الناتجة عن إذابة الحمض اتجاهًا مشابهًا بين المجموعات التجريبية. لوحظت نسبة Ca/P مستقرة أو متزايدة بعد ذوبان الحمض في المجموعات المشعة، مع انخفاض Ca المنطلق في المحلول الحمضي.

Translated Description (French)

Une augmentation de la résistance à l'acide de l'émail dentaire, ainsi que des changements morphologiques et structurels produits par l'irradiation au laser Er :YAG, a été rapportée. Pour évaluer les changements chimiques associés à la résistance à l'acide de l'émail traité au laser Er :YAG. Méthodes. Quarante-huit échantillons d'émail ont été divisés en 4 groupes (n = 12). Groupe I (contrôle) ; les groupes II, III et IV ont été irradiés avec Er :YAG à 100 mJ (12,7 J/cm(2)), 200 mJ (25,5 J/cm(2)) et 300 mJ (38,2 J/cm(2)), respectivement. Il y avait des différences significatives dans la composition des groupes irradiés (à l'exception du chlore) et dans la quantité de calcium libérée. Les changements chimiques associés à une augmentation de la résistance à l'acide de l'émail traité avec Er : laser YAG ont montré un schéma clair de post-tirradiation caractérisé par une diminution de C at.% et une augmentation de O, P et Ca at.% et aucun changement de Cl at.%. Un rapport Ca/P accru après irradiation laser Er :YAG a été associé à l'utilisation de densités d'énergie laser plus élevées. Les changements chimiques produits par la dissolution acide ont montré une tendance similaire parmi les groupes expérimentaux. Un rapport Ca/P stable ou augmenté après dissolution de l'acide a été observé dans les groupes irradiés, avec une réduction du Ca libéré dans la solution acide.

Translated Description (Spanish)

Se ha reportado un aumento en la resistencia ácida del esmalte dental, así como cambios morfológicos y estructurales producidos por la irradiación láser Er:YAG, para evaluar los cambios químicos asociados a la resistencia ácida del esmalte tratado con láser Er:YAG. Métodos. Cuarenta y ocho muestras de esmalte se dividieron en 4 grupos (n = 12). Grupo I (control); Los grupos II, III y IV se irradiaron con Er:YAG a 100 mJ (12.7 J/cm(2)), 200 mJ (25.5 J/cm(2)) y 300 mJ (38.2 J/cm(2)), respectivamente. Hubo diferencias significativas en la composición de los grupos irradiados (con la excepción del cloro) y en la cantidad de calcio liberado. Los cambios químicos asociados con un aumento en la resistencia al ácido del esmalte tratado con láser Er:YAG mostraron un patrón claro de postirradiación caracterizado por una disminución en C at.% y un aumento en O, P y Ca at.% y sin cambios en Cl at.%. Un aumento de la relación Ca/P después de la irradiación con láser Er:YAG se asoció con el uso de densidades de energía láser más altas. Los cambios químicos producidos por la disolución ácida mostraron una tendencia similar entre los grupos experimentales. Se observó una relación Ca/P estable o aumentada después de la disolución ácida en los grupos irradiados, con reducción de Ca liberado en la solución ácida.

Files

501357.pdf.pdf

Files (15.9 kB)

⚠️ Please wait a few minutes before your translated files are ready ⚠️ Note: Some files might be protected thus translations might not work.
Name Size Download all
md5:176b664486d4cc3a5d23f54ebd90959a
15.9 kB
Preview Download

Additional details

Additional titles

Translated title (Arabic)
التغيرات الكيميائية المرتبطة بزيادة مقاومة الأحماض في المينا المشعة بالليزر YAG
Translated title (French)
Changements chimiques associés à une résistance accrue à l'acide de l'émail irradié au laser Er :YAG
Translated title (Spanish)
Cambios químicos asociados con el aumento de la resistencia al ácido del esmalte irradiado con láser Er:YAG

Identifiers

Other
https://openalex.org/W2058426039
DOI
10.1155/2014/501357

Is supplement to
https://openalex.org/W862679594 (Other)
https://openalex.org/W3157748779 (Other)
https://openalex.org/W2939358970 (Other)
https://openalex.org/W2886952586 (Other)
https://openalex.org/W2364539061 (Other)
https://openalex.org/W2170325754 (Other)
https://openalex.org/W2080451171 (Other)
https://openalex.org/W2046158925 (Other)
https://openalex.org/W2020893790 (Other)
https://openalex.org/W2012540211 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Mexico

References

  • https://openalex.org/W1912989677
  • https://openalex.org/W1920971922
  • https://openalex.org/W1966843519
  • https://openalex.org/W1979257495
  • https://openalex.org/W1988360723
  • https://openalex.org/W2003874520
  • https://openalex.org/W2012016817
  • https://openalex.org/W2013595670
  • https://openalex.org/W2014931656
  • https://openalex.org/W2035115452
  • https://openalex.org/W2041935275
  • https://openalex.org/W2051784723
  • https://openalex.org/W2058883845
  • https://openalex.org/W2060635625
  • https://openalex.org/W2062652628
  • https://openalex.org/W2064237938
  • https://openalex.org/W2067113969
  • https://openalex.org/W2073221560
  • https://openalex.org/W2080952534
  • https://openalex.org/W2084090335
  • https://openalex.org/W2084810021
  • https://openalex.org/W2085804429
  • https://openalex.org/W2116003583
  • https://openalex.org/W2614850163
  • https://openalex.org/W4235466046
  • https://openalex.org/W4293103692