Influence of the surface finish on corrosion resistance of stainless steels through machining and remelting on weld bead
Creators
- 1. Universidade Estadual do Maranhão
- 2. Instituto Federal do Maranhão
- 3. Universidade Federal de Uberlândia
Description
The TIG Dressing technique has been widely used for repairing cracks in welded structures when subjected to mechanical forces that induce localized fatigue, leading to the collapse during operation. However, this technique has not been used for studies in structures susceptible to corrosion. In addition to changing the microstructure, it is expected that this technique increases the corrosion resistance of the edge of the weld bead which is a vulnerable region to corrosion. Moreover, the machining technique has been widely used to improve the workpieces finishing and/or structures that have been subjected to repair by welding, improving the surface roughness, increasing the corrosion resistance of these structures when subjected to aggressive environments. Thus, this work will study the effects of finishing techniques using machining and welding on the edge of the weld bead joints of 410D ferritic stainless steels, making an evaluation by mass loss in the samples which will be subjected to corrosion by immersion in NaCl containing medium. It is expected that the finishing techniques can relieve tensile stresses increasing the corrosion resistance.
Translated Descriptions
⚠️
This is an automatic machine translation with an accuracy of 90-95%
Translated Description (Arabic)
تم استخدام تقنية تضميد TIG على نطاق واسع لإصلاح الشقوق في الهياكل الملحومة عند تعرضها لقوى ميكانيكية تحفز التعب الموضعي، مما يؤدي إلى الانهيار أثناء التشغيل. ومع ذلك، لم يتم استخدام هذه التقنية للدراسات في الهياكل المعرضة للتآكل. بالإضافة إلى تغيير البنية المجهرية، من المتوقع أن تزيد هذه التقنية من مقاومة التآكل لحافة خرزة اللحام التي تعد منطقة عرضة للتآكل. علاوة على ذلك، تم استخدام تقنية التشغيل الآلي على نطاق واسع لتحسين تشطيب قطع العمل و/أو الهياكل التي تعرضت للإصلاح عن طريق اللحام، وتحسين خشونة السطح، وزيادة مقاومة التآكل لهذه الهياكل عند تعرضها لبيئات عدوانية. وبالتالي، سيدرس هذا العمل آثار تقنيات التشطيب باستخدام الآلات واللحام على حافة وصلات خرزة اللحام من الفولاذ المقاوم للصدأ الحديدي 410D، مما يجعل التقييم عن طريق فقدان الكتلة في العينات التي ستتعرض للتآكل عن طريق الغمر في وسط يحتوي على كلوريد الصوديوم. من المتوقع أن تخفف تقنيات التشطيب من إجهادات الشد مما يزيد من مقاومة التآكل.Translated Description (French)
La technique de pansement TIG a été largement utilisée pour réparer les fissures dans les structures soudées lorsqu'elles sont soumises à des forces mécaniques qui induisent une fatigue localisée, conduisant à l'effondrement pendant le fonctionnement. Cependant, cette technique n'a pas été utilisée pour des études dans des structures sensibles à la corrosion. En plus de changer la microstructure, on s'attend à ce que cette technique augmente la résistance à la corrosion du bord du cordon de soudure qui est une région vulnérable à la corrosion. De plus, la technique d'usinage a été largement utilisée pour améliorer la finition des pièces et/ou des structures qui ont été soumises à une réparation par soudage, améliorer la rugosité de surface, augmenter la résistance à la corrosion de ces structures lorsqu'elles sont soumises à des environnements agressifs. Ainsi, ce travail étudiera les effets des techniques de finition par usinage et soudage sur le bord des joints de cordon de soudure des aciers inoxydables ferritiques 410D, en faisant une évaluation par perte de masse dans les échantillons qui seront soumis à la corrosion par immersion dans un milieu contenant du NaCl. On s'attend à ce que les techniques de finition puissent soulager les contraintes de traction en augmentant la résistance à la corrosion.Translated Description (Spanish)
La técnica de apósito TIG se ha utilizado ampliamente para reparar grietas en estructuras soldadas cuando se someten a fuerzas mecánicas que inducen fatiga localizada, lo que lleva al colapso durante la operación. Sin embargo, esta técnica no se ha utilizado para estudios en estructuras susceptibles a la corrosión. Además de cambiar la microestructura, se espera que esta técnica aumente la resistencia a la corrosión del borde del cordón de soldadura, que es una región vulnerable a la corrosión. Además, la técnica de mecanizado ha sido ampliamente utilizada para mejorar el acabado de las piezas de trabajo y/o estructuras que han sido sometidas a reparación por soldadura, mejorando la rugosidad de la superficie, aumentando la resistencia a la corrosión de estas estructuras cuando se someten a ambientes agresivos. Así, en este trabajo se estudiarán los efectos de las técnicas de acabado mediante mecanizado y soldadura en el borde de las uniones de cordón de soldadura de aceros inoxidables ferríticos 410D, realizando una evaluación por pérdida de masa en las muestras que serán sometidas a corrosión por inmersión en medio que contiene NaCl. Se espera que las técnicas de acabado puedan aliviar los esfuerzos de tracción aumentando la resistencia a la corrosión.Files
pdf.pdf
Files
(257 Bytes)
| Name | Size | Download all |
|---|---|---|
|
md5:5d98d69a65b87c202a2284e0e0484f46
|
257 Bytes | Preview Download |
Additional details
Additional titles
- Translated title (Arabic)
- تأثير تشطيب السطح على مقاومة التآكل للفولاذ المقاوم للصدأ من خلال التشغيل الآلي وإعادة الصهر على حبة اللحام
- Translated title (French)
- Influence de l'état de surface sur la résistance à la corrosion des aciers inoxydables par usinage et refusion sur cordon de soudure
- Translated title (Spanish)
- Influencia del acabado superficial en la resistencia a la corrosión de los aceros inoxidables a través del mecanizado y la refundición en el cordón de soldadura
Identifiers
- Other
- https://openalex.org/W2948975327
- DOI
- 10.4025/actascitechnol.v41i1.37732
References
- https://openalex.org/W1533123219
- https://openalex.org/W1570947856
- https://openalex.org/W2025141095
- https://openalex.org/W2065347342
- https://openalex.org/W2070461455
- https://openalex.org/W2082547771
- https://openalex.org/W2084833666
- https://openalex.org/W2099880065
- https://openalex.org/W2157782975
- https://openalex.org/W2499250562
- https://openalex.org/W2519021100
- https://openalex.org/W2525232824
- https://openalex.org/W2588365074
- https://openalex.org/W2596558426
- https://openalex.org/W2625298257
- https://openalex.org/W2997020658
- https://openalex.org/W387685221
- https://openalex.org/W570959715
- https://openalex.org/W812584461