A Study of 1-Benzyl-3-phenyl-2-thiourea as an Effective Steel Corrosion Inhibitor in 1.0 M HCl Solution

Creators

  • 1. Hue University
  • 2. University of Da Nang

Description

1-Benzyl-3-phenyl-2-thiourea (BPTU) was studied as a steel corrosion inhibitor in 1.0 M HCl solution. Experimental methods were conducted including potentiodynamic polarization measurement (PPM), electrochemical impedance spectroscopy (EIS), and scanning electron microscopy (SEM) analysis. Quantum calculations were performed at B3LYP/6-311G(d,p). Hexamethylenetetramine (URO) was selected for comparison with BPTU. The results showed that BPTU with the concentration of 2 × 10−4 M and at the temperature of 30°C could protect the steel surface with the highest inhibition efficiency of 94.99% and 94.30% according to EIS and PPM, respectively. High temperature decreased BPTU's ability to inhibit the steel corrosion. The adsorption of BPTU on the steel surface is followed by the modified Langmuir isotherm. Quantum chemical calculations showed that the thiourea functional group is the main adsorption center of BPTU. The experimental results are completely consistent with theoretical calculations.

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

تمت دراسة 1 -بنزيل-3 -فينيل-2 -ثيو يوريا (BPTU) كمثبط للتآكل الفولاذي في محلول 1.0 م من حمض الهيدروكلوريك. تم إجراء طرق تجريبية بما في ذلك قياس الاستقطاب الديناميكي (PPM)، والتحليل الطيفي للمعاوقة الكهروكيميائية (EIS)، وتحليل المجهر الإلكتروني الماسح (SEM). تم إجراء الحسابات الكمية في B3LYP/6-311 G(d,p). تم اختيار سداسي ميثيلين رباعي الأمين (URO) للمقارنة مع BPTU. أظهرت النتائج أن BPTU بتركيز 2 × 10−4 م وعند درجة حرارة 30 درجة مئوية يمكن أن يحمي سطح الفولاذ بأعلى كفاءة تثبيط بنسبة 94.99 ٪ و 94.30 ٪ وفقًا لـ EIS و PPM، على التوالي. أدت درجة الحرارة العالية إلى انخفاض قدرة BPTU على تثبيط تآكل الفولاذ. يتبع امتزاز BPTU على سطح الفولاذ متساوي حرارة Langmuir المعدل. أظهرت الحسابات الكيميائية الكمومية أن المجموعة الوظيفية للثيوريا هي مركز الامتزاز الرئيسي لـ BPTU. تتوافق النتائج التجريبية تمامًا مع الحسابات النظرية.

Translated Description (French)

La 1-benzyl-3-phényl-2-thiourée (BPTU) a été étudiée comme inhibiteur de corrosion de l'acier dans une solution de HCl 1,0 M. Des méthodes expérimentales ont été menées, notamment la mesure de la polarisation potentiodynamique (PPM), la spectroscopie d'impédance électrochimique (EIS) et l'analyse par microscopie électronique à balayage (MEB). Des calculs quantiques ont été effectués à B3LYP/6-311G(d,p). L'hexaméthylènetétramine (URO) a été sélectionnée pour être comparée à la BPTU. Les résultats ont montré que le BPTU à la concentration de 2 × 10−4 M et à la température de 30 °C pouvait protéger la surface de l'acier avec l'efficacité d'inhibition la plus élevée de 94,99 % et 94,30 % selon l'EIS et le PPM, respectivement. La température élevée a diminué la capacité de BPTU à inhiber la corrosion de l'acier. L'adsorption de BPTU sur la surface d'acier est suivie de l'isotherme de Langmuir modifiée. Les calculs chimiques quantiques ont montré que le groupe fonctionnel thiourée est le principal centre d'adsorption de BPTU. Les résultats expérimentaux sont tout à fait cohérents avec les calculs théoriques.

Translated Description (Spanish)

Se estudió 1-bencil-3-fenil-2-tiourea (BPTU) como inhibidor de la corrosión del acero en solución de HCl 1.0 M. Se llevaron a cabo métodos experimentales que incluyeron medición de polarización potenciodinámica (PPM), espectroscopía de impedancia electroquímica (EIS) y análisis de microscopía electrónica de barrido (SEM). Los cálculos cuánticos se realizaron en B3LYP/6-311G(d,p). Se seleccionó hexametilentetramina (URO) para la comparación con BPTU. Los resultados mostraron que BPTU con la concentración de 2 × 10−4 M y a la temperatura de 30 ° C podría proteger la superficie de acero con la mayor eficiencia de inhibición de 94.99% y 94.30% según EIS y PPM, respectivamente. La alta temperatura disminuyó la capacidad de BPTU para inhibir la corrosión del acero. La adsorción de BPTU en la superficie del acero es seguida por la isoterma de Langmuir modificada. Los cálculos químicos cuánticos mostraron que el grupo funcional tiourea es el principal centro de adsorción de BPTU. Los resultados experimentales son completamente consistentes con los cálculos teóricos.

Files

5519411.pdf.pdf

Files (15.9 kB)

⚠️ Please wait a few minutes before your translated files are ready ⚠️ Note: Some files might be protected thus translations might not work.
Name Size Download all
md5:75e8281c3ee6cc2fb04ab6d6015395e6
15.9 kB
Preview Download

Additional details

Additional titles

Translated title (Arabic)
دراسة 1 -بنزيل-3 -فينيل-2 -ثيووريا كمثبط فعال للتآكل الفولاذي في محلول حمض الهيدروكلوريك 1.0 م
Translated title (French)
Une étude de la 1-benzyl-3-phényl-2-thiourée en tant qu'inhibiteur efficace de la corrosion de l'acier dans une solution de HCl 1,0 M
Translated title (Spanish)
Un estudio de 1-bencil-3-fenil-2-tiourea como inhibidor eficaz de la corrosión del acero en solución de HCl 1,0 M

Identifiers

Other
https://openalex.org/W3162677676
DOI
10.1155/2021/5519411

Is supplement to
https://openalex.org/W576020941 (Other)
https://openalex.org/W4382060113 (Other)
https://openalex.org/W2952367897 (Other)
https://openalex.org/W2952189174 (Other)
https://openalex.org/W2414169739 (Other)
https://openalex.org/W2390872968 (Other)
https://openalex.org/W2314523112 (Other)
https://openalex.org/W2060784808 (Other)
https://openalex.org/W1970719926 (Other)
https://openalex.org/W1966522134 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Vietnam

References

  • https://openalex.org/W1828240244
  • https://openalex.org/W1975400049
  • https://openalex.org/W1975743712
  • https://openalex.org/W1976525951
  • https://openalex.org/W1981262922
  • https://openalex.org/W1989285709
  • https://openalex.org/W1995898257
  • https://openalex.org/W1996276148
  • https://openalex.org/W2002185861
  • https://openalex.org/W2004600818
  • https://openalex.org/W2006441761
  • https://openalex.org/W2008708918
  • https://openalex.org/W2012750404
  • https://openalex.org/W2035599335
  • https://openalex.org/W2037376242
  • https://openalex.org/W2040278300
  • https://openalex.org/W2041675487
  • https://openalex.org/W2044148901
  • https://openalex.org/W2045822286
  • https://openalex.org/W2052486442
  • https://openalex.org/W2056848679
  • https://openalex.org/W2060329468
  • https://openalex.org/W2064963641
  • https://openalex.org/W2071789277
  • https://openalex.org/W2078805639
  • https://openalex.org/W2082984671
  • https://openalex.org/W2086708818
  • https://openalex.org/W2088877194
  • https://openalex.org/W2128332443
  • https://openalex.org/W2129372591
  • https://openalex.org/W2145461981
  • https://openalex.org/W2161093362
  • https://openalex.org/W2169927586
  • https://openalex.org/W2169986484
  • https://openalex.org/W2279945746
  • https://openalex.org/W2293781874
  • https://openalex.org/W2346085258
  • https://openalex.org/W2416624910
  • https://openalex.org/W2550925725
  • https://openalex.org/W2737581811
  • https://openalex.org/W2755770859
  • https://openalex.org/W2760228162
  • https://openalex.org/W2775168676
  • https://openalex.org/W2792847257
  • https://openalex.org/W2801417041
  • https://openalex.org/W2803548388
  • https://openalex.org/W2808351127
  • https://openalex.org/W2923783744
  • https://openalex.org/W2946666423
  • https://openalex.org/W2955679600
  • https://openalex.org/W3008797083
  • https://openalex.org/W3009709379
  • https://openalex.org/W3081136244
  • https://openalex.org/W4247007873