Study of Catalytic Capacity of ZnO Nano Particles by Blue Methylen
- 1. VNU University of Science
Description
ZnO nanostructures were prepared by hydrothermal method starting from Zn(CH3COO)2, citric acid and NaOH. SEM images indicated that the samples have a spherical shape consisting of small wires with a diameter of about 50 nm. It is seen that the samples have large surface areas and will be attractive for applications like catalyst, catalyst sensors and solar cells. In this report, photocatalytic capacity of ZnO nanoparticles was investigated by time-dependent absorption spectra of 10 mg/L blue methylen solution. The results show that catalysis was almost complete after 120 minutes. The effects of pH value on the morphology and photoluminescence properties of the samples have also been investigated. [DOI: 10.1380/ejssnt.2011.512]
Translated Descriptions
⚠️
This is an automatic machine translation with an accuracy of 90-95%
Translated Description (Arabic)
تم تحضير البنى النانوية لأكسيد الزنك بطريقة حرارية مائية بدءًا من الزنك(CH3COO)2 وحمض الستريك و هيدروكسيد الصوديوم. أشارت صور SEM إلى أن العينات لها شكل كروي يتكون من أسلاك صغيرة يبلغ قطرها حوالي 50 نانومتر. من الملاحظ أن العينات لها مساحات سطحية كبيرة وستكون جذابة لتطبيقات مثل المحفز وأجهزة استشعار المحفز والخلايا الشمسية. في هذا التقرير، تم فحص القدرة التحفيزية الضوئية لجسيمات ZnO النانوية من خلال أطياف الامتصاص المعتمدة على الوقت لمحلول الميثيلين الأزرق 10 مجم/لتر. تظهر النتائج أن التحفيز قد اكتمل تقريبًا بعد 120 دقيقة. كما تم التحقيق في آثار قيمة الرقم الهيدروجيني على خصائص التشكل والتلألؤ الضوئي للعينات. [DOI: 10.1380/ejssnt.2011.512]Translated Description (French)
Les nanostructures de ZnO ont été préparées par méthode hydrothermale à partir de Zn(CH3COO)2, d'acide citrique et de NaOH. Les images MEB ont indiqué que les échantillons ont une forme sphérique composée de petits fils d'un diamètre d'environ 50 nm. On voit que les échantillons ont de grandes surfaces et seront attrayants pour des applications comme le catalyseur, les capteurs de catalyseur et les cellules solaires. Dans ce rapport, la capacité photocatalytique des nanoparticules de ZnO a été étudiée par des spectres d'absorption dépendant du temps de 10 mg/L de solution de méthylène bleu. Les résultats montrent que la catalyse était presque terminée après 120 minutes. Les effets de la valeur du pH sur la morphologie et les propriétés de photoluminescence des échantillons ont également été étudiés. [DOI : 10.1380/ejssnt.2011.512]Translated Description (Spanish)
Las nanoestructuras de ZnO se prepararon mediante un método hidrotérmico a partir de Zn(CH3COO)2, ácido cítrico y NaOH. Las imágenes SEM indicaron que las muestras tienen una forma esférica que consiste en pequeños alambres con un diámetro de aproximadamente 50 nm. Se observa que las muestras tienen grandes áreas de superficie y serán atractivas para aplicaciones como catalizador, sensores de catalizador y células solares. En este informe, la capacidad fotocatalítica de las nanopartículas de ZnO se investigó mediante espectros de absorción dependientes del tiempo de 10 mg/L de solución de metileno azul. Los resultados muestran que la catálisis estaba casi completa después de 120 minutos. También se han investigado los efectos del valor de pH sobre la morfología y las propiedades de fotoluminiscencia de las muestras. [DOI: 10.1380/ejssnt.2011.512]Files
_pdf.pdf
Files
(1.3 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:9d1edcea7ab674fd7c69078b570c94c1
|
1.3 MB | Preview Download |
Additional details
Additional titles
- Translated title (Arabic)
- دراسة القدرة التحفيزية لجسيمات النانو ZnO بواسطة الميثيلين الأزرق
- Translated title (French)
- Étude de la capacité catalytique des nanoparticules de ZnO par le méthylène bleu
- Translated title (Spanish)
- Estudio de la capacidad catalítica de las nanopartículas de ZnO mediante metileno azul
Identifiers
- Other
- https://openalex.org/W1969558299
- DOI
- 10.1380/ejssnt.2011.512
References
- https://openalex.org/W1963808574
- https://openalex.org/W2167504062