A facile hydrothermal approach for catalytic and optical behavior of tin oxide- graphene (SnO2/G) nanocomposite

Creators

  • 1. National Defence University of Malaysia
  • 2. AMET University
  • 3. University of Malaya
  • 4. Rutgers, The State University of New Jersey
  • 5. Bangladesh University

Description

A cost-effective, facile hydrothermal approach was made for the synthesis of SnO2/graphene (Gr) nano-composites. XRD diffraction spectra clearly confirmed the presence of tetragonal crystal system of SnO2 which was maintaining its structure in both pure and composite materials' matrix. The stretching and bending vibrations of the functional groups were analyzed using FTIR analysis. FESEM images illustrated the surface morphology and the texture of the synthesized sample. HRTEM images confirmed the deposition of SnO2 nanoparticles over the surface of graphene nano-sheets. Raman Spectroscopic analysis was carried out to confirm the in-plane blending of SnO2 and graphene inside the composite matrix. The photocatalytic performance of the synthesized sample under UV irradiation using methylene blue dye was observed. Incorporation of grapheme into the SnO2 sample had increased the photocatalytic activity compared with the pure SnO2 sample. The electrochemical property of the synthesized sample was evaluated.

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

تم اتباع نهج حراري مائي سهل وفعال من حيث التكلفة لتوليف المركبات النانوية SnO2/الجرافين (Gr). أكدت أطياف حيود XRD بوضوح وجود نظام بلوري رباعي الزوايا لـ SnO2 والذي كان يحافظ على هيكله في كل من مصفوفة المواد النقية والمركبة. تم تحليل اهتزازات التمدد والانحناء للمجموعات الوظيفية باستخدام تحليل FTIR. أوضحت صور FESEM مورفولوجيا السطح وملمس العينة المركبة. أكدت صور HRTEM ترسب جسيمات SnO2 النانوية على سطح صفائح الجرافين النانوية. تم إجراء تحليل رامان الطيفي لتأكيد المزج داخل الطائرة بين SnO2 والجرافين داخل المصفوفة المركبة. لوحظ الأداء التحفيزي الضوئي للعينة المركبة تحت الأشعة فوق البنفسجية باستخدام صبغة الميثيلين الزرقاء. أدى دمج الجرافيم في عينة SnO2 إلى زيادة النشاط التحفيزي الضوئي مقارنة بعينة SnO2 النقية. تم تقييم الخاصية الكهروكيميائية للعينة المركبة.

Translated Description (French)

Une approche hydrothermale rentable et facile a été réalisée pour la synthèse de nanocomposites SnO2/graphène (Gr). Les spectres de diffraction XRD ont clairement confirmé la présence d'un système cristallin tétragonal de SnO2 qui maintenait sa structure dans la matrice des matériaux purs et composites. Les vibrations d'étirement et de flexion des groupes fonctionnels ont été analysées à l'aide de l'analyse IRTF. Les images FESEM illustrent la morphologie de surface et la texture de l'échantillon synthétisé. Les images HRTEM ont confirmé le dépôt de nanoparticules de SnO2 sur la surface des nanofeuilles de graphène. Une analyse spectroscopique Raman a été réalisée pour confirmer le mélange dans le plan de SnO2 et de graphène à l'intérieur de la matrice composite. La performance photocatalytique de l'échantillon synthétisé sous irradiation UV à l'aide de colorant bleu de méthylène a été observée. L'incorporation de graphème dans l'échantillon de SnO2 avait augmenté l'activité photocatalytique par rapport à l'échantillon de SnO2 pur. La propriété électrochimique de l'échantillon synthétisé a été évaluée.

Translated Description (Spanish)

Se realizó un enfoque hidrotermal fácil y rentable para la síntesis de nanocompuestos de SnO2/grafeno (Gr). Los espectros de difracción XRD confirmaron claramente la presencia de un sistema cristalino tetragonal de SnO2 que mantenía su estructura en la matriz de materiales puros y compuestos. Las vibraciones de estiramiento y flexión de los grupos funcionales se analizaron mediante análisis FTIR. Las imágenes FESEM ilustraron la morfología de la superficie y la textura de la muestra sintetizada. Las imágenes de HRTEM confirmaron la deposición de nanopartículas de SnO2 sobre la superficie de las nanohojas de grafeno. Se llevó a cabo un análisis espectroscópico Raman para confirmar la mezcla en el plano de SnO2 y grafeno dentro de la matriz compuesta. Se observó el rendimiento fotocatalítico de la muestra sintetizada bajo irradiación UV utilizando colorante azul de metileno. La incorporación de grafema en la muestra de SnO2 había aumentado la actividad fotocatalítica en comparación con la muestra de SnO2 puro. Se evaluó la propiedad electroquímica de la muestra sintetizada.

Files

journal.pone.0202694&type=printable.pdf

Files (13.2 MB)

⚠️ Please wait a few minutes before your translated files are ready ⚠️ Note: Some files might be protected thus translations might not work.
Name Size Download all
md5:e4b8e0d19ab1d8b9c34639b6a1ee8275
13.2 MB
Preview Download

Additional details

Additional titles

Translated title (Arabic)
نهج حراري مائي سهل للسلوك الحفاز والبصري لأكسيد القصدير - الجرافين (SnO2/G) المركب النانوي
Translated title (French)
Une approche hydrothermique facile pour le comportement catalytique et optique du nanocomposite oxyde d'étain-graphène (SnO2/G)
Translated title (Spanish)
Un enfoque hidrotérmico fácil para el comportamiento catalítico y óptico del nanocompuesto de óxido de estaño-grafeno (SnO2/G)

Identifiers

Other
https://openalex.org/W2895456830
DOI
10.1371/journal.pone.0202694

Is supplement to
https://openalex.org/W4224078161 (Other)
https://openalex.org/W2389190295 (Other)
https://openalex.org/W2365787373 (Other)
https://openalex.org/W2239791767 (Other)
https://openalex.org/W2203859666 (Other)
https://openalex.org/W2202470948 (Other)
https://openalex.org/W2081438754 (Other)
https://openalex.org/W2043701887 (Other)
https://openalex.org/W2022456520 (Other)
https://openalex.org/W1995481507 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Malaysia

References

  • https://openalex.org/W1190026296
  • https://openalex.org/W1964877755
  • https://openalex.org/W1974899246
  • https://openalex.org/W1984775992
  • https://openalex.org/W1985152113
  • https://openalex.org/W1985728643
  • https://openalex.org/W1989981819
  • https://openalex.org/W1991418576
  • https://openalex.org/W1995701417
  • https://openalex.org/W2014935324
  • https://openalex.org/W2019283458
  • https://openalex.org/W2025661778
  • https://openalex.org/W2028535387
  • https://openalex.org/W2031231753
  • https://openalex.org/W2031913137
  • https://openalex.org/W2034724723
  • https://openalex.org/W2051739870
  • https://openalex.org/W2060870583
  • https://openalex.org/W2061373025
  • https://openalex.org/W2070716620
  • https://openalex.org/W2071625206
  • https://openalex.org/W2080548892
  • https://openalex.org/W2083893864
  • https://openalex.org/W2087582258
  • https://openalex.org/W2088918550
  • https://openalex.org/W2101977779
  • https://openalex.org/W2105685140
  • https://openalex.org/W2110863248
  • https://openalex.org/W2118492507
  • https://openalex.org/W2121772044
  • https://openalex.org/W2123510746
  • https://openalex.org/W2124855231
  • https://openalex.org/W2125284466
  • https://openalex.org/W2126148458
  • https://openalex.org/W2128654538
  • https://openalex.org/W2132535652
  • https://openalex.org/W2328661249
  • https://openalex.org/W2472113000
  • https://openalex.org/W2522914535
  • https://openalex.org/W2584314363
  • https://openalex.org/W2588343144
  • https://openalex.org/W2591707311
  • https://openalex.org/W2606559953
  • https://openalex.org/W2743914162
  • https://openalex.org/W2747794228
  • https://openalex.org/W2751704495
  • https://openalex.org/W2768991438
  • https://openalex.org/W2770655856
  • https://openalex.org/W2771263447
  • https://openalex.org/W2782603040
  • https://openalex.org/W2791063019
  • https://openalex.org/W2793390164
  • https://openalex.org/W2794118468
  • https://openalex.org/W2800762918
  • https://openalex.org/W2803980415
  • https://openalex.org/W329677749