Assessment of Fracture Resistance of PEEK and Fibre Posts of the Endodontically Treated Teeth

Creators

  • 1. King Khalid University
  • 2. Riphah International University
  • 3. Dow University of Health Sciences

Description

This in vitro study aimed to compare the fracture resistance between pressed custom-made polyetheretherketone (PEEK) post and core and fibre reinforced post and composite core. A total of 40 single rooted extracted teeth were selected, endodontically treated, and prepared to receive the posts. Specimens were randomly divided into two main groups (n=20/group): group 1, (PEEK); group 2, fibre post. PEEK post was manufactured with a computer-aided design/computer-aided manufacturing system further divided into four sub groups (P7, P12, F7, F12) based on lengths 7 and 12 mm at which the posts were cemented. All posts were cemented with self-adhesive resin cement, and specimens were stored in 0.1% thymol solution during the experiment at all the times except during preparation and testing. A universal testing machine was used to measure the fracture resistance. The fracture resistance values (mean and SD, in newtons) were 1255N (P7), 1562N (P12), 1065N (F7), and 1384N (F12). Only P12 exhibited a significant difference (p,0.05). The turkey test showed an association between failure mode and post and- core material. In the remaining groups, most failures were nonrepairable and related to fracture. Customized post-and-cores of PEEK exhibited good mechanical performance. Their fracture resistance was comparable to that observed for fibre posts.

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

تهدف هذه الدراسة المختبرية إلى مقارنة مقاومة الكسر بين عمود البولي إيثر كيتون المضغوط حسب الطلب (PEEK) والقلب والقلب المقوى بالألياف والقلب المركب. تم اختيار ما مجموعه 40 من الأسنان المستخرجة أحادية الجذر، ومعالجتها بطانة الأسنان، وإعدادها لاستقبال الأعمدة. تم تقسيم العينات بشكل عشوائي إلى مجموعتين رئيسيتين (n=20/group): المجموعة 1، (نظرة خاطفة) ؛ المجموعة 2، منشور الألياف. تم تصنيع عمود PEEK باستخدام تصميم بمساعدة الكمبيوتر/نظام تصنيع بمساعدة الكمبيوتر مقسمًا أيضًا إلى أربع مجموعات فرعية (P7 و P12 و F7 و F12) بناءً على الأطوال 7 و 12 مم التي تم فيها تثبيت الأعمدة بالأسمنت. تم تدعيم جميع الأعمدة بأسمنت راتنجي ذاتي اللصق، وتم تخزين العينات في محلول ثيمول 0.1 ٪ أثناء التجربة في جميع الأوقات باستثناء أثناء التحضير والاختبار. تم استخدام آلة اختبار عالمية لقياس مقاومة الكسر. كانت قيم مقاومة الكسر (المتوسط و SD، بالنيوتن) 1255N (P7)، 1562N (P12)، 1065N (F7)، و 1384N (F12). أظهر P12 فقط فرقًا كبيرًا (ص،0.05). أظهر اختبار تركيا وجود ارتباط بين وضع الفشل ومادة ما بعد النواة. في المجموعات المتبقية، كانت معظم حالات الفشل غير قابلة للإصلاح ومتعلقة بالكسر. أظهر ما بعد ونواة PEEK المخصصة أداءً ميكانيكيًا جيدًا. كانت مقاومتهم للكسر مماثلة لتلك التي لوحظت في أعمدة الألياف.

Translated Description (French)

Cette étude in vitro visait à comparer la résistance à la fracture entre un poteau en polyétheréthercétone (PEEK) pressé sur mesure et un poteau renforcé par des fibres et un noyau composite. Au total, 40 dents extraites à racine unique ont été sélectionnées, traitées par endodontie et préparées pour recevoir les poteaux. Les échantillons ont été divisés au hasard en deux groupes principaux (n=20/groupe) : groupe 1, (PEEK) ; groupe 2, fibre post. LE POTEAU PEEK a été fabriqué avec un système de conception assistée par ordinateur/de fabrication assistée par ordinateur divisé en quatre sous-groupes (P7, P12, F7, F12) en fonction des longueurs 7 et 12 mm auxquelles les poteaux ont été cimentés. Tous les poteaux ont été cimentés avec du ciment de résine auto-adhésif, et les échantillons ont été stockés dans une solution de thymol à 0,1% pendant l'expérience à tout moment, sauf pendant la préparation et les tests. Une machine d'essai universelle a été utilisée pour mesurer la résistance à la rupture. Les valeurs de résistance à la rupture (moyenne et écart-type, en newtons) étaient de 1255N (P7), 1562N (P12), 1065N (F7) et 1384N (F12). Seule P12 présentait une différence significative (p,0,05). Le test de la dinde a montré une association entre le mode de défaillance et le matériau post-noyau. Dans les autres groupes, la plupart des défaillances étaient irréparables et liées à une fracture. Les post-noyaux personnalisés de PEEK ont montré de bonnes performances mécaniques. Leur résistance à la rupture était comparable à celle observée pour les poteaux de fibres.

Translated Description (Spanish)

Este estudio in vitro tuvo como objetivo comparar la resistencia a la fractura entre el poste de polieteretercetona (PEEK) prensado y el núcleo y el poste reforzado con fibra y el núcleo compuesto. Se seleccionaron un total de 40 dientes extraídos de una sola raíz, se trataron endodónticamente y se prepararon para recibir los postes. Las muestras se dividieron aleatoriamente en dos grupos principales (n=20/grupo): grupo 1, (PEEK); grupo 2, poste de fibra. El poste PEEK se fabricó con un sistema de diseño asistido por ordenador/fabricación asistida por ordenador dividido en cuatro subgrupos (P7, P12, F7, F12) en función de las longitudes de 7 y 12 mm en las que se cementaron los postes. Todos los postes se cementaron con cemento de resina autoadhesiva y las muestras se almacenaron en solución de timol al 0,1% durante el experimento en todo momento, excepto durante la preparación y la prueba. Se utilizó una máquina de prueba universal para medir la resistencia a la fractura. Los valores de resistencia a la fractura (media y SD, en newtons) fueron 1255N (P7), 1562N (P12), 1065N (F7) y 1384N (F12). Solo P12 mostró una diferencia significativa (p,0.05). La prueba de pavo mostró una asociación entre el modo de falla y el material de poste y núcleo. En los grupos restantes, la mayoría de las fallas no fueron reparables y se relacionaron con fracturas. Los postes y núcleos personalizados de PEEK MOSTRARON UN buen rendimiento mecánico. Su resistencia a la fractura fue comparable a la observada para los postes de fibra.

Files

20 GOTAM 1 22.pdf.pdf

Files (198.1 kB)

⚠️ Please wait a few minutes before your translated files are ready ⚠️ Note: Some files might be protected thus translations might not work.
Name Size Download all
md5:673054f3074f1e1f9436d25aeddeb7e6
198.1 kB
Preview Download

Additional details

Additional titles

Translated title (Arabic)
تقييم مقاومة الكسر لأعمدة PEEK والألياف للأسنان المعالجة بطانة الأسنان
Translated title (French)
Évaluation de la résistance aux fractures des poteaux en PEEK et en fibres des dents traitées par endodontie
Translated title (Spanish)
Evaluación de la resistencia a la fractura de los postes de PEEK y fibra de los dientes tratados endodónticamente

Identifiers

Other
https://openalex.org/W4224139673
DOI
10.37358/mp.22.1.5573

Is supplement to
https://openalex.org/W4389573601 (Other)
https://openalex.org/W4309244196 (Other)
https://openalex.org/W3002944756 (Other)
https://openalex.org/W2767905081 (Other)
https://openalex.org/W2607306954 (Other)
https://openalex.org/W2606417881 (Other)
https://openalex.org/W2563877375 (Other)
https://openalex.org/W2356596750 (Other)
https://openalex.org/W2073027460 (Other)
https://openalex.org/W1595823417 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Pakistan

References

  • https://openalex.org/W1711420795
  • https://openalex.org/W1985165519
  • https://openalex.org/W2063374401
  • https://openalex.org/W2314338708
  • https://openalex.org/W2496918064
  • https://openalex.org/W2888813532
  • https://openalex.org/W2897266651
  • https://openalex.org/W2936610174
  • https://openalex.org/W2998142809
  • https://openalex.org/W3014264380
  • https://openalex.org/W3082139417
  • https://openalex.org/W3090074367
  • https://openalex.org/W3090226644
  • https://openalex.org/W3119580243
  • https://openalex.org/W3130460073
  • https://openalex.org/W3163112803
  • https://openalex.org/W3186629186
  • https://openalex.org/W3211674974
  • https://openalex.org/W4205287393
  • https://openalex.org/W4210749526
  • https://openalex.org/W4214772657
  • https://openalex.org/W4214855946
  • https://openalex.org/W4287444013