Influence of Palm Oil Fuel Ash and W/B Ratios on Compressive Strength, Water Permeability, and Chloride Resistance of Concrete
- 1. King Mongkut's University of Technology Thonburi
- 2. Burapha University
Description
This research studies the effects of W/B ratios and palm oil fuel ash (POFA) on compressive strength, water permeability, and chloride resistance of concrete. POFA was ground until the particles retained on sieve number 325 were less than 5% by weight. POFA was used to partially replace OPC at rates of 15, 25, and 35% by weight of binder. The water to binder (W/B) ratios of concrete were 0.40 and 0.50. The compressive strength, water permeability, and chloride resistance of concrete were investigated up to 90 days. The results showed that POFA concrete with W/B ratio of 0.40 had the compressive strengths ranging from 45.8 to 55.9 MPa or 82–94% of OPC concrete at 90 days, while POFA concrete with W/B ratio of 0.50 had the compressive strengths of 33.9–41.9 MPa or 81–94% of OPC concrete. Furthermore, the compressive strength of concrete incorporation of ground POFA at 15% was the same as OPC concrete. The water permeability coefficient and the chloride ion penetration of POFA concrete were lower than OPC concrete when both types of concrete had the same compressive strengths. The findings also indicated that water permeability and chloride ion penetration of POFA concrete were significantly reduced compared to OPC concrete.
Translated Descriptions
⚠️
This is an automatic machine translation with an accuracy of 90-95%
Translated Description (Arabic)
يدرس هذا البحث آثار نسب W/B ورماد وقود زيت النخيل (POFA) على قوة الانضغاط ونفاذية المياه ومقاومة كلوريد الخرسانة. تم طحن POFA حتى كانت الجسيمات المحتجزة على الغربال رقم 325 أقل من 5 ٪ بالوزن. تم استخدام POFA لاستبدال OPC جزئيًا بمعدلات 15 و 25 و 35 ٪ من وزن المادة الرابطة. كانت نسب الماء إلى المادة الرابطة (W/B) للخرسانة 0.40 و 0.50. تم فحص قوة الانضغاط ونفاذية الماء ومقاومة الكلوريد للخرسانة لمدة تصل إلى 90 يومًا. أظهرت النتائج أن خرسانة POFA ذات نسبة W/B البالغة 0.40 كانت لها مقاومة انضغاط تتراوح من 45.8 إلى 55.9 ميجا باسكال أو 82-94 ٪ من خرسانة OPC في 90 يومًا، في حين أن خرسانة POFA ذات نسبة W/B البالغة 0.50 كانت لها مقاومة انضغاط تتراوح بين 33.9-41.9 ميجا باسكال أو 81-94 ٪ من خرسانة OPC. علاوة على ذلك، كانت قوة الانضغاط لدمج الخرسانة في POFA الأرضي بنسبة 15 ٪ هي نفسها خرسانة OPC. كان معامل نفاذية المياه واختراق أيون الكلوريد لخرسانة POFA أقل من خرسانة OPC عندما كان لكلا النوعين من الخرسانة نفس مقاومة الانضغاط. أشارت النتائج أيضًا إلى أن نفاذية المياه واختراق أيون الكلوريد لخرسانة POFA قد انخفض بشكل كبير مقارنة بخرسانة OPC.Translated Description (French)
Cette recherche étudie les effets des rapports E/B et des cendres de carburant à l'huile de palme (POFA) sur la résistance à la compression, la perméabilité à l'eau et la résistance au chlorure du béton. Le POFA a été broyé jusqu'à ce que les particules retenues sur le tamis numéro 325 soient inférieures à 5% en poids. Le POFA a été utilisé pour remplacer partiellement l'OPC à des taux de 15, 25 et 35 % en poids de liant. Les rapports eau/liant (E/B) du béton étaient de 0,40 et 0,50. La résistance à la compression, la perméabilité à l'eau et la résistance au chlorure du béton ont été étudiées jusqu'à 90 jours. Les résultats ont montré que le béton POFA avec un rapport E/B de 0,40 avait des résistances à la compression allant de 45,8 à 55,9 MPa ou 82–94% du béton OPC à 90 jours, tandis que le béton POFA avec un rapport E/B de 0,50 avait des résistances à la compression de 33,9-41,9 MPa ou 81-94% du béton OPC. De plus, la résistance à la compression de l'incorporation de béton de POFA au sol à 15% était la même que celle du béton OPC. Le coefficient de perméabilité à l'eau et la pénétration des ions chlorure du béton POFA étaient inférieurs à ceux du béton OPC lorsque les deux types de béton avaient les mêmes résistances à la compression. Les résultats ont également indiqué que la perméabilité à l'eau et la pénétration des ions chlorure du béton POFA étaient significativement réduites par rapport au béton OPC.Translated Description (Spanish)
Esta investigación estudia los efectos de las proporciones W/B y las cenizas de combustible de aceite de palma (POFA) sobre la resistencia a la compresión, la permeabilidad al agua y la resistencia al cloruro del concreto. Los POFA se molieron hasta que las partículas retenidas en el tamiz número 325 fueron inferiores al 5% en peso. Se utilizó POFA para reemplazar parcialmente OPC a tasas de 15, 25 y 35% en peso de aglutinante. Las relaciones de agua a aglutinante (W/B) del concreto fueron 0.40 y 0.50. Se investigó la resistencia a la compresión, la permeabilidad al agua y la resistencia al cloruro del concreto hasta 90 días. Los resultados mostraron que el concreto POFA con relación W/B de 0.40 tuvo las resistencias a la compresión que van de 45.8 a 55.9 MPa o 82–94% del concreto OPC a los 90 días, mientras que el concreto POFA con relación W/B de 0.50 tuvo las resistencias a la compresión de 33.9-41.9 MPa o 81-94% del concreto OPC. Además, la resistencia a la compresión de la incorporación de concreto de POFA molido al 15% fue la misma que la del concreto OPC. El coeficiente de permeabilidad al agua y la penetración de iones cloruro del hormigón POFA fueron inferiores a los del hormigón OPC cuando ambos tipos de hormigón tenían las mismas resistencias a la compresión. Los hallazgos también indicaron que la permeabilidad al agua y la penetración de iones cloruro del hormigón POFA se redujeron significativamente en comparación con el hormigón OPC.Files
4927640.pdf.pdf
Files
(16.0 kB)
| Name | Size | Download all |
|---|---|---|
|
md5:30a55c91a781820eaf9c801a43c65340
|
16.0 kB | Preview Download |
Additional details
Additional titles
- Translated title (Arabic)
- تأثير نسب رماد وقود زيت النخيل و W/B على مقاومة الانضغاط ونفاذية الماء ومقاومة كلوريد الخرسانة
- Translated title (French)
- Influence des cendres de carburant d'huile de palme et des rapports E/B sur la résistance à la compression, la perméabilité à l'eau et la résistance au chlorure du béton
- Translated title (Spanish)
- Influencia de la ceniza de combustible de aceite de palma y las relaciones W/B en la resistencia a la compresión, la permeabilidad al agua y la resistencia al cloruro del concreto
Identifiers
- Other
- https://openalex.org/W2734026633
- DOI
- 10.1155/2017/4927640
References
- https://openalex.org/W1967580270
- https://openalex.org/W1968383247
- https://openalex.org/W1972604909
- https://openalex.org/W1986358422
- https://openalex.org/W1987086141
- https://openalex.org/W1990668054
- https://openalex.org/W1995384721
- https://openalex.org/W2005157077
- https://openalex.org/W2012847578
- https://openalex.org/W2026176002
- https://openalex.org/W2029762110
- https://openalex.org/W2033894052
- https://openalex.org/W2041481060
- https://openalex.org/W2044569169
- https://openalex.org/W2051927107
- https://openalex.org/W2059094448
- https://openalex.org/W2064000939
- https://openalex.org/W2068205672
- https://openalex.org/W2068279981
- https://openalex.org/W2075357706
- https://openalex.org/W2091563345
- https://openalex.org/W2093201013
- https://openalex.org/W2101177906
- https://openalex.org/W2107150495
- https://openalex.org/W2125410485
- https://openalex.org/W2134767709
- https://openalex.org/W2153947164
- https://openalex.org/W2169575903
- https://openalex.org/W856688047