Dopant Concentration and Effective Atomic Number of Copper-Doped Potassium Borate Glasses
Creators
- 1. King Abdulaziz University
- 2. University of Technology Malaysia
Description
Copper-doped (0.5 mol%) and undoped potassium borate glasses have been prepared by the composition of (100- x )H 3 BO 3 + x K 2 CO 3 , where 10 ≤ x ≤ 30 mol % by the traditional melting quenching method. The structural pattern of glasses with different composition has been identified by X-ray diffraction (XRD). The glow curves were analysed to determine various characterizations of the TLDs. Identification of the compositions and concentrations and effective atomic number of undoped and doped potassium borate glass was carried out using scanning electron microscope analysis (SEM). The dopant concentrations are found to be 0.25 mol%, while Z eff are 11.42 and 10.48 for Cu-doped and undoped potassium borate glasses, respectively.
Translated Descriptions
⚠️
This is an automatic machine translation with an accuracy of 90-95%
Translated Description (Arabic)
تم تحضير نظارات بورات البوتاسيوم النحاسية المنشطة (0.5 مول%) وغير المنشطة بتركيبة (100 - x )H 3 BO 3 + x K 2 CO 3 ، حيث 10 ≤ x ≤ 30 مول % بطريقة التبريد بالصهر التقليدية. تم تحديد النمط الهيكلي للنظارات ذات التركيب المختلف من خلال حيود الأشعة السينية (XRD). تم تحليل منحنيات التوهج لتحديد الخصائص المختلفة لنطاقات TLD. تم تحديد التركيبات والتركيزات والعدد الذري الفعال لزجاج بورات البوتاسيوم غير المنشط والمخدر باستخدام تحليل المجهر الإلكتروني الماسح (SEM). تم العثور على تركيزات الإشابة بنسبة 0.25 ٪ مول، في حين أن Z eff هي 11.42 و 10.48 لنظارات بورات البوتاسيوم المشابة وغير المشابة، على التوالي.Translated Description (French)
Des verres de borate de potassium dopés au cuivre (0,5 mol%) et non dopés ont été préparés par la composition de (100- x )H 3 BO 3 + x K 2 CO 3 , où 10 ≤ x ≤ 30 mol % par le procédé traditionnel de trempe par fusion. Le motif structurel des verres de composition différente a été identifié par diffraction des rayons X (DRX). Les courbes de luminescence ont été analysées pour déterminer diverses caractérisations des TLD. L'identification des compositions et des concentrations et du numéro atomique effectif du verre de borate de potassium non dopé et dopé a été réalisée par analyse au microscope électronique à balayage (MEB). Les concentrations de dopant sont trouvées à 0,25 mol%, tandis que Z eff sont de 11,42 et 10,48 pour les verres de borate de potassium dopés au cuivre et non dopés, respectivement.Translated Description (Spanish)
Los vidrios de borato de potasio dopados con cobre (0,5% en moles) y no dopados se han preparado mediante la composición de (100- x )H 3 BO 3 + x K 2 CO 3 , donde 10 ≤ x ≤ 30% en moles mediante el método tradicional de enfriamiento por fusión. El patrón estructural de los vidrios con diferente composición se ha identificado mediante difracción de rayos X (XRD). Las curvas de brillo se analizaron para determinar varias caracterizaciones de los TLD. La identificación de las composiciones y concentraciones y el número atómico efectivo del vidrio de borato de potasio no dopado y dopado se llevó a cabo utilizando un análisis de microscopio electrónico de barrido (SEM). Se encuentra que las concentraciones de dopante son 0.25 mol%, mientras que Z eff son 11.42 y 10.48 para vidrios de borato de potasio dopados con Cu y no dopados, respectivamente.Files
278934.pdf.pdf
Files
(15.8 kB)
| Name | Size | Download all |
|---|---|---|
|
md5:187f175e581a7d261e664fe0b9005f7c
|
15.8 kB | Preview Download |
Additional details
Additional titles
- Translated title (Arabic)
- تركيز الإشابة والعدد الذري الفعال لنظارات بورات البوتاسيوم المشابة بالنحاس
- Translated title (French)
- Concentration de dopant et nombre atomique effectif de verres de borate de potassium dopés au cuivre
- Translated title (Spanish)
- Concentración de dopante y número atómico efectivo de vasos de borato de potasio dopados con cobre
Identifiers
- Other
- https://openalex.org/W2169651627
- DOI
- 10.1155/2013/278934
References
- https://openalex.org/W1996909089
- https://openalex.org/W2053419463
- https://openalex.org/W2065609059
- https://openalex.org/W2068008300
- https://openalex.org/W2087627318
- https://openalex.org/W2092571568
- https://openalex.org/W2101841914