A new method for assessment of nickel-titanium endodontic instrument surface roughness using field emission scanning electronic microscope

Creators

  • 1. Ho Chi Minh City Medicine and Pharmacy University
  • 2. Vietnam National University Ho Chi Minh City

Description

Abstract Background To introduce a new method for measurement of surface roughness of the endodontic instrument, before and after instrumentation, using the Field Emission Scanning Electronic Microscope (FE-SEM) combined with the ImageJ software. Methods Twenty J-shape resin blocks were divided into two groups, ten blocks of each group. Simulated root canal inside the resin block was 16 mm length, 60 0 angle of curvature, and radius of 4.5 mm. Ten WaveOne Gold Primary and 10 Reciproc Blue R25 instruments were used for root canal instrumentation. The instruments were scanned before and after instrumentation with special molds made to ensure the same areas at the point located 3 mm from the tips of the instruments using the FE-SEM. These scanned images were analyzed using the ImageJ. The arithmetical mean roughness (R a ), root mean square roughness (R q ), and the average distance between the highest peak and lowest valley in each sampling length (R z ) were calculated by ImageJ for quantitative analyses. The paired-t test was performed to analyze the data using the SPSS 22.0 at the significance of .05. Results Almost all surface roughness values were decreased. However, these decreases were not statistically significant ( P > .05). Conclusions The FE-SEM combined with the ImageJ was the reliable and appropriate modality for measurement surface roughness of instruments.

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

خلفية مجردة لتقديم طريقة جديدة لقياس خشونة سطح الأداة اللبية، قبل وبعد الأجهزة، باستخدام المجهر الإلكتروني لمسح الانبعاثات الميدانية (FE - SEM) جنبًا إلى جنب مع برنامج ImageJ. الطرق تم تقسيم عشرين كتلة راتنج على شكل حرف J إلى مجموعتين، عشر كتل من كل مجموعة. كان طول قناة الجذر المحاكاة داخل كتلة الراتنج 16 مم، و 60 0 زاوية انحناء، ونصف قطر 4.5 مم. تم استخدام عشرة أدوات WaveOne Gold Primary و 10 أدوات Reciproc Blue R25 لأجهزة قناة الجذر. تم مسح الأدوات ضوئيًا قبل وبعد الأجهزة باستخدام قوالب خاصة مصنوعة لضمان نفس المناطق عند النقطة الواقعة على بعد 3 مم من أطراف الأدوات باستخدام FE - SEM. تم تحليل هذه الصور الممسوحة ضوئيًا باستخدام ImageJ. تم حساب متوسط الخشونة الحسابية (R a )، ومتوسط خشونة الجذر التربيعي (R q )، ومتوسط المسافة بين أعلى قمة وأدنى وادٍ في كل طول أخذ عينات (R z ) بواسطة ImageJ للتحليلات الكمية. تم إجراء الاختبار المزدوج لتحليل البيانات باستخدام SPSS 22.0 بقيمة 0.05. النتائج انخفضت جميع قيم خشونة السطح تقريبًا. ومع ذلك، لم تكن هذه الانخفاضات ذات دلالة إحصائية ( P > .05). الاستنتاجات كانت FE - SEM جنبًا إلى جنب مع ImageJ هي الطريقة الموثوقة والمناسبة لقياس خشونة سطح الأدوات.

Translated Description (French)

Résumé Contexte Introduire une nouvelle méthode de mesure de la rugosité de surface de l'instrument endodontique, avant et après instrumentation, à l'aide du microscope électronique à balayage par émission de champ (FE-SEM) combiné au logiciel ImageJ. Méthodes Vingt blocs de résine en forme de J ont été divisés en deux groupes, dix blocs de chaque groupe. Le canal radiculaire simulé à l'intérieur du bloc de résine avait une longueur de 16 mm, un angle de courbure de 60 0 et un rayon de 4,5 mm. Dix instruments WaveOne Gold Primary et 10 Reciproc Blue R25 ont été utilisés pour l'instrumentation du canal radiculaire. Les instruments ont été scannés avant et après l'instrumentation avec des moules spéciaux fabriqués pour assurer les mêmes zones au point situé à 3 mm des pointes des instruments à l'aide du FE-SEM. Ces images numérisées ont été analysées à l'aide de l'ImageJ. La rugosité moyenne arithmétique (R a ), la rugosité moyenne quadratique (R q ) et la distance moyenne entre le pic le plus élevé et la vallée la plus basse dans chaque longueur d'échantillonnage (R z ) ont été calculées par ImageJ pour des analyses quantitatives. Le test paird-t a été effectué pour analyser les données à l'aide du SPSS 22.0 à la signification de 0,05. Résultats Presque toutes les valeurs de rugosité de surface ont été diminuées. Cependant, ces diminutions n'étaient pas statistiquement significatives ( P > 0,05). Conclusions Le FE-SEM combiné à l'ImageJ était la modalité fiable et appropriée pour mesurer la rugosité de surface des instruments.

Translated Description (Spanish)

Antecedentes abstractos Introducir un nuevo método para la medición de la rugosidad de la superficie del instrumento de endodoncia, antes y después de la instrumentación, utilizando el Microscopio Electrónico de Escaneo de Emisión de Campo (FE-SEM) combinado con el software ImageJ. Métodos Se dividieron veinte bloques de resina en forma de J en dos grupos, diez bloques de cada grupo. El conducto radicular simulado dentro del bloque de resina tenía una longitud de 16 mm, un ángulo de curvatura de 60 ° y un radio de 4,5 mm. Se utilizaron diez instrumentos WaveOne Gold Primary y 10 Reciproc Blue R25 para la instrumentación del conducto radicular. Los instrumentos se escanearon antes y después de la instrumentación con moldes especiales hechos para asegurar las mismas áreas en el punto ubicado a 3 mm de las puntas de los instrumentos utilizando el FE-SEM. Estas imágenes escaneadas se analizaron utilizando el ImageJ. ImageJ calculó la rugosidad media aritmética (R a), la rugosidad media cuadrática (R q ) y la distancia media entre el pico más alto y el valle más bajo en cada longitud de muestreo (R z ) para los análisis cuantitativos. La prueba de t pareada se realizó para analizar los datos utilizando el SPSS 22.0 en la significación de .05. Resultados Casi todos los valores de rugosidad superficial disminuyeron. Sin embargo, estas disminuciones no fueron estadísticamente significativas ( P > 0,05). Conclusiones El FE-SEM combinado con el ImageJ fue la modalidad fiable y adecuada para la medición de la rugosidad superficial de los instrumentos.

Files

s12903-020-01233-0.pdf

Files (1.1 MB)

⚠️ Please wait a few minutes before your translated files are ready ⚠️ Note: Some files might be protected thus translations might not work.
Name Size Download all
md5:5743f29d60ac722f7f3df08633bdb62e
1.1 MB
Preview Download

Additional details

Additional titles

Translated title (Arabic)
طريقة جديدة لتقييم خشونة سطح أداة النيكل والتيتانيوم اللبية باستخدام المجهر الإلكتروني لمسح الانبعاثات الميدانية
Translated title (French)
Une nouvelle méthode d'évaluation de la rugosité de surface des instruments endodontiques nickel-titane à l'aide d'un microscope électronique à balayage à émission de champ
Translated title (Spanish)
Un nuevo método para la evaluación de la rugosidad de la superficie del instrumento de endodoncia de níquel-titanio utilizando microscopio electrónico de barrido de emisión de campo

Identifiers

Other
https://openalex.org/W3082673630
DOI
10.1186/s12903-020-01233-0

Is supplement to
https://openalex.org/W562823126 (Other)
https://openalex.org/W2993874308 (Other)
https://openalex.org/W2469134140 (Other)
https://openalex.org/W2165392093 (Other)
https://openalex.org/W2143942744 (Other)
https://openalex.org/W2113699753 (Other)
https://openalex.org/W2106037662 (Other)
https://openalex.org/W2045782830 (Other)
https://openalex.org/W1972557159 (Other)
https://openalex.org/W1530419332 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Vietnam

References

  • https://openalex.org/W1977814578
  • https://openalex.org/W1980192651
  • https://openalex.org/W1989716051
  • https://openalex.org/W1997110196
  • https://openalex.org/W2000965098
  • https://openalex.org/W2010903965
  • https://openalex.org/W2040201209
  • https://openalex.org/W2088204210
  • https://openalex.org/W2110088992
  • https://openalex.org/W2119645544
  • https://openalex.org/W2125331886
  • https://openalex.org/W2137710435
  • https://openalex.org/W2169128735
  • https://openalex.org/W2339623593
  • https://openalex.org/W2528018715
  • https://openalex.org/W2550056290
  • https://openalex.org/W2761925876
  • https://openalex.org/W2787448931
  • https://openalex.org/W2807891114
  • https://openalex.org/W2852297668
  • https://openalex.org/W2914574376
  • https://openalex.org/W2925516319
  • https://openalex.org/W2997693358
  • https://openalex.org/W3021538646