Enhanced Photocatalytic Activity of ZrO<sub>2</sub>-SiO<sub>2</sub>Nanoparticles by Platinum Doping

Creators

  • 1. King Abdulaziz University
  • 2. Central Metallurgical Research and Development Institute

Description

ZrO 2 -SiO 2 mixed oxides were prepared via the sol-gel method. Photo-assisted deposition was utilized for doping the prepared mixed oxide with 0.1, 0.2, 0.3, and 0.4 wt% of Pt. XRD spectra showed that doping did not result in the incorporation of Pt within the crystal structure of the material. UV-reflectance spectrometry showed that the band gap of ZrO 2 -SiO 2 decreased from 3.04 eV to 2.48 eV with 0.4 wt% Pt doping. The results show a specific surface area increase of 20%. Enhanced photocatalysis of Pt/ZrO 2 -SiO 2 was successfully tested on photo degradation of cyanide under illumination of visible light. 100% conversion was achieved within 20 min with 0.3 wt% of Pt doped ZrO 2 -SiO 2 .

⚠️ This is an automatic machine translation with an accuracy of 90-95%

Translated Description (Arabic)

تم تحضير أكاسيد ZrO 2 - SiO 2 المختلطة عبر طريقة sol - gel. تم استخدام الترسيب بمساعدة الصور لتخدير الأكسيد المختلط المحضر بنسبة 0.1 و 0.2 و 0.3 و 0.4 ٪ بالوزن من Pt. أظهرت أطياف XRD أن المنشطات لم تؤدي إلى دمج Pt داخل البنية البلورية للمادة. أظهر قياس طيف الانعكاس للأشعة فوق البنفسجية أن فجوة النطاق ZrO 2 - SiO 2 انخفضت من 3.04 إلكترون فولت إلى 2.48 إلكترون فولت مع 0.4% بالوزن من المنشطات. تظهر النتائج زيادة محددة في مساحة السطح بنسبة 20 ٪. تم اختبار التحفيز الضوئي المحسن لـ Pt/ZrO 2 - SiO 2 بنجاح على التحلل الضوئي للسيانيد تحت إضاءة الضوء المرئي. تم تحقيق تحويل 100 ٪ في غضون 20 دقيقة مع 0.3 ٪ بالوزن من Pt doped ZrO 2 - SiO 2 .

Translated Description (French)

Les oxydes mixtes ZrO 2 -SiO 2 ont été préparés par la méthode sol-gel. Le dépôt photo-assisté a été utilisé pour doper l'oxyde mixte préparé avec 0,1, 0,2, 0,3 et 0,4 % en poids de Pt. Les spectres XRD ont montré que le dopage n'entraînait pas l'incorporation de Pt dans la structure cristalline du matériau. La spectrométrie de réflectance UV a montré que la bande interdite de ZrO 2 -SiO 2 diminuait de 3,04 eV à 2,48 eV avec un dopage au Pt de 0,4 % en poids. Les résultats montrent une augmentation de surface spécifique de 20%. La photocatalyse améliorée de Pt/ZrO 2 -SiO 2 a été testée avec succès sur la photodégradation du cyanure sous éclairage de lumière visible. Une conversion de 100 % a été obtenue en 20 min avec 0,3 % en poids de ZrO 2 -SiO 2 dopé au Pt.

Translated Description (Spanish)

Los óxidos mixtos de ZrO 2 -SiO 2 se prepararon mediante el método sol-gel. La deposición fotoasistida se utilizó para dopar el óxido mixto preparado con 0,1, 0,2, 0,3 y 0,4% en peso de Pt. Los espectros de XRD mostraron que el dopaje no dio como resultado la incorporación de Pt dentro de la estructura cristalina del material. La espectrometría de reflectancia UV mostró que la brecha de banda de ZrO 2 -SiO 2 disminuyó de 3.04 eV a 2.48 eV con 0.4% enpeso de dopaje de Pt. Los resultados muestran un aumento de la superficie específica del 20%. La fotocatálisis mejorada de Pt/ZrO 2 -SiO 2 se probó con éxito en la fotodegradación del cianuro bajo iluminación de luz visible. Se logró una conversión del 100% en 20 minutos con un 0,3% en peso de ZrO 2 -SiO 2 dopado con Pt.

Files

812097.pdf.pdf

Files (16.0 kB)

⚠️ Please wait a few minutes before your translated files are ready ⚠️ Note: Some files might be protected thus translations might not work.
Name Size Download all
md5:6483e1fb1837ed21960ed7ff62156a47
16.0 kB
Preview Download

Additional details

Additional titles

Translated title (Arabic)
النشاط التحفيزي الضوئي المعزز لجسيمات ZrO<sub>2 -</sub>SiO<sub>2</sub>النانوية عن طريق المنشطات البلاتينية
Translated title (French)
Activité photocatalytique améliorée des nanoparticules de ZrO<sub>2</sub>-SiO<sub>2</sub> par dopage au platine
Translated title (Spanish)
Actividad fotocatalítica mejorada de nanopartículas de ZrO<sub>2</sub>-SiO<sub>2</sub> mediante dopaje con platino

Identifiers

Other
https://openalex.org/W2079793930
DOI
10.1155/2013/812097

Is supplement to
https://openalex.org/W4387258219 (Other)
https://openalex.org/W4380084229 (Other)
https://openalex.org/W3210285899 (Other)
https://openalex.org/W2971454175 (Other)
https://openalex.org/W2569071712 (Other)
https://openalex.org/W2329571231 (Other)
https://openalex.org/W2083707091 (Other)
https://openalex.org/W2080109862 (Other)
https://openalex.org/W2063384240 (Other)
https://openalex.org/W1976504271 (Other)

GreSIS Basics Section

Is Global South Knowledge
Yes
Country
Egypt

References

  • https://openalex.org/W1978393358
  • https://openalex.org/W1980541902
  • https://openalex.org/W1986616666
  • https://openalex.org/W1988126186
  • https://openalex.org/W2006143727
  • https://openalex.org/W2007270911
  • https://openalex.org/W2010589586
  • https://openalex.org/W2014375453
  • https://openalex.org/W2022071849
  • https://openalex.org/W2022535464
  • https://openalex.org/W2025890066
  • https://openalex.org/W2040438240
  • https://openalex.org/W2047820155
  • https://openalex.org/W2065544922
  • https://openalex.org/W2068421871
  • https://openalex.org/W2069340746
  • https://openalex.org/W2073382960
  • https://openalex.org/W2082659557
  • https://openalex.org/W2086150366
  • https://openalex.org/W2109089548
  • https://openalex.org/W2119585240
  • https://openalex.org/W4211254512